海洋环境下7B04铝合金腐蚀损伤演化规律研究 |
王刚,金平,谭晓明,王德 |
海军航空工程学院青岛校区航空机械系 青岛 266041 |
|
RESEARCH ON CORROSION DAMAGE EVOLVEMENT RULE OF 7B04 ALUMINUM ALLOY UNDER OCEAN ENVIRONMENT |
WANG Gang, JIN Ping, TAN Xiaoming, WANG De |
Department of Aeronautical Mechanism, Naval Aeronautical Engineering Academy Qingdao Branch, Qingdao 266041 |
[1] Zhang Y H, Lv G Z, Ren K L, et al. The evolution rhythm of surface corrosion damage of LY12CZ aluminum in varied environments [J]. Acta Aeronaut. Astronaut. Sin., 2007, 28(1): 142-145 (张有宏, 吕国志, 任克亮等. 不同环境下LY122CZ铝合金表面腐蚀损伤演化规律研究[J]. 航空学报, 2007, 28(1): 142-145)[2] Xu H P, Liu H C, Zhu L Q. Relation between pitting corrosion behavior and exposed area of high strength aluminum alloys in neutral salt spray [J]. J. Aeronaut. Mater., 2010, 30(4): 59-64 (徐火平, 刘慧丛, 朱立群等. 盐雾环境中高强铝合金点腐蚀行为与暴露面积的关系[J]. 航空材料学报, 2010, 30(4): 59-64)[3] Mu Z T, Xiong Y P. Distribution of corrosion damage of high strength aluminum alloys [J]. Mater. Mech. Eng., 2002, 26(4): 14-16 (穆志韬, 熊玉平. 高强度铝合金的腐蚀损伤分布规律研究[J]. 机械工程材料, 2002, 26(4): 14-16)[4] Mu Z T, Zeng B Y, Jin P, et al. Fatigue of Helicopter Structures [M]. Beijing: National Defense Industry Press, 2009 (穆志韬, 曾本银, 金平等. 直升机结构疲劳[M]. 北京: 国防工业出版社, 2009)[5] Liu W T, Li Y H. The Calendar Life System Evaluation Technology of Aircraft Structures [M]. Beijing: Aviation Industry Press, 2004 (刘文珽, 李玉海. 飞机结构日历寿命体系评定技术[M]. 北京: 航空工业出版社, 2004)[6] Zhang Y H. Corrosion damage and fatigue life of aircraft structure[D]. Xi$^{\prime}$an: Northwestern Polytechnical University, 2007 (张有宏. 飞机结构的腐蚀损伤及其对寿命的影响[D]. 西安: 西北工业大学, 2007)[7] Codaro E N, Nakazato R Z, Horovistiz A L. An image processing method for morphology characterization and pitting corrosion evaluation[J]. Mater. Sci. Eng, 2002, A334(2): 298-306[8] Chen Q Z, Cui C J. Probability distribution and variations of corrosion damage of LY12CZ aluminum alloys [J]. Equip. Environ. Eng., 2005, 12(3): 1-6 (陈群志, 崔常京. LY12CZ铝合金腐蚀损伤的概率分布及变化规律[J]. 装备环境工程, 2005, 12(3): 1-6)[9] Sheikh A K, Boah J K, Hansen D A. Statistical modeling of pitting corrosion and pipeline reliability[J]. Corrosion, 1990, 46(3): 190-197[10] Zhang F G, Ye B, Gao Y J. Study of corrosion damage dynamics law of aluminum alloy material [J]. New Technol. New Process, 2010, 11: 58-59 (张福高, 叶斌, 高艳军. 铝合金材料腐蚀损伤动力学规律研究[J]. 新技术新工艺, 2010, 11: 58-59) |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|