磷对低碳钢耐大气腐蚀性能的影响研究

中国腐蚀与防护学报

2007, Vol. 27

Issue (3): 137-141

研究报告

本期目录 | 过刊浏览

磷对低碳钢耐大气腐蚀性能的影响研究

贾书君;刘清友;汪兵

钢铁研究总院结构材料研究所

Research on the Influences of Phosphorus on Corrosion resistance in Low Carbon Steels

;;;

钢铁研究总院结构材料研究所

全文: PDF(309 KB)

摘要: 通过周浸加速腐蚀实验、扫描电镜、拉曼光谱分析等方法，研究了磷含量对低碳钢耐大气腐蚀性能的影响。结果表明，磷能明显提高材料的耐大气的腐蚀性能，这种作用在腐蚀初期尤为显著。其原因是：偏聚在材料表面上的磷原子在水和氧的作用下水解，生成一种致密性较高磷酸盐，并且能均匀覆盖在基体表面的空洞和裂纹处，阻碍了水和氧的通过，使基体免遭进一步的腐蚀。并且H2PO4-能够加速锈层中Fe2+向 Fe3+的转化、使腐蚀初期反应快速进行、阻止铁锈粒子长大，使腐蚀生成物颗粒细小、结构致密。促进了致密、稳定、均匀的保护膜形成。

关键词 ：耐大气腐蚀性能, 磷酸盐, 保护性锈层

Abstract：The effects of phosphorus on corrosion resistance of low carbon steels have been investigated by cyclic corrosion test、SEM and micro-Raman analysis. The results indicate that phosphorus can increase corrosion resistance of low carbon steels especially at the early stage of atmospheric corrosion. The reason is :with the effect of water and oxygen, the phosphorus enriched on the face of steels was hydrolyzed ,then phosphate was formed .This kind of phosphate cover on the cranny and holes in rust and resist water and oxygen’s passing. Moreover, the can accelerate the air oxidation of Fe2+ to Fe3+ and the formation of stable rust . As a result , the corrosion resistance of high phosphorus steels was improved .

Key words： corrosion resistance phosphate protective rust

收稿日期: 2005-12-28

ZTFLH:

TG172

通讯作者: 贾书君 E-mail: jiajsj504@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	贾书君
	刘清友
	汪兵
44.8K

引用本文:

贾书君; 刘清友; 汪兵 . 磷对低碳钢耐大气腐蚀性能的影响研究[J]. 中国腐蚀与防护学报, 2007, 27(3): 137-141 .
. Research on the Influences of Phosphorus on Corrosion resistance in Low Carbon Steels. J Chin Soc Corr Pro, 2007, 27(3): 137-141 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I3/137

[1]PerhovJ,Grman D,Svoboda M,Patscheider J,et al.Microstructur-al aspects of phosphorus grain boundary segregation in low alloysteels[J].Mater.Letters,2001,47(1):44-49
[2]Zhang D B,Wu C J,Yang R,et al.Grain boundary segregation of Pin Fe-P and Fe-P-Ce alloys and effect on their brittleness[J].Acta Metall.Sin.,1991,27(2):A111-A114(张东彬,吴承建,杨让等.Fe-P与Fe-P-Ce合金中的晶界磷偏聚及其对脆性的影响[J].金属学报,1991,27(2):A111-A114)
[3]Masato Yamashita,Hiroo Nagano,Toshihei Misawa,et al.Structure ofprotective rust layers formed on weathering steels by long-termexpo-sure in the industrial atmospheres of Japan and North America[J].ISIJ International,1998,38(3):285-290
[4]Chen X Q,Chang WS,Kong X D,et al.Effect of phosphoric segrega-tion on the pitting in carbon steels[J].J.Chin.Soc.Corros.Prot.,2001,21(4):193-199(陈学群,常万顺,孔小东等.碳钢中磷的偏析对坑孔腐蚀的影响[J].中国腐蚀与防护学报,2001,21(4):193-199)
[5]Res.Gp of phosphorus Segregation(Institute of Metal Research,Ac-ademia Sinica).Observation of phosphorus segregation and its influ-ence upon embrittlement[J].Acta Metall.Sini.,1981,17(2):124-129(中国科学院金属研究所磷偏析研究组.磷在钢中的偏析及钢的脆性[J].金属学报,1981,17(2):124-129)
[6]Balasubramaniam R.On the corrosion resistance of the Delhi iron pil-lar[J].Corros.Sci.,2000,42(12):2103-2129

[1]	崔学军，刘春海，李明田，林修洲，刘元洪. 工艺参数对AZ31镁合金磷化膜耐蚀性能及表面形貌的影响[J]. 中国腐蚀与防护学报, 2012, 32(6): 507-512.
[2]	崔学军,周吉学,王修春. 镁合金AZ31表面无铬磷酸盐转化膜的制备、结构及性能[J]. 中国腐蚀与防护学报, 2012, 32(1): 13-17.
[3]	谢斌,赖川,邹立科,何林芯,伍一峥,黄炎俊,相阳光. O,O'-二（环己基）二硫代磷酸-N,N-二乙铵对Q235钢在硫酸溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 225-230.
[4]	王博,卢凯,王建景,姜茂发,王德永,刘承军. 模拟工业大气条件下高锰耐候钢的腐蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(4): 333-336.
[5]	林晶; 阎永贵; 陈光章; 马力; 钱建华 . 应用原子力显微镜研究硫酸盐还原菌对A3钢的腐蚀[J]. 中国腐蚀与防护学报, 2007, 27(2): 70-.

Viewed

Full text

Abstract

Cited

Shared

Discussed