SiO2-K2SiO3涂层对空间材料Kaphton的防护行为研究

张蕾;严川伟;李绮

中科院金属研究所（南区）

PROTECTIVE EFFECTS OF SIO2-K2SIO3 ORGANIC-INORGANIC COMPOSITE COATINGS FOR THE SPACECRAFT

Zhang Lei;Yan Chuanwei;Li Qi

中科院金属研究所（南区）

全文: PDF(146 KB)

摘要: 在微波电离型原子氧（AO）源地面模拟设备中对空间材料Kapton及SiO2-K2SiO3无机-有机复合涂层进行原子氧剥蚀效应试验。用扫描电镜(SEM)、光电子能谱(XPS)、红外光谱(FT-IR)、X射线衍射光谱（XRD）和LAMBDA-9分光光度计，对在模拟原子氧(AO)环境中Kapton及在其表面涂覆的涂层所发生的侵蚀与防护作用进行了表征研究。AO对Kapton表现了较严重的侵蚀作用，表面呈现粗糙，失去原有光滑和透明。而施加的SiO2-K2SiO3涂层，经AO辐照后，表面却变化甚少。实验表明，该涂层对AO辐照有较强的防护效果，有较好的空间稳定性，能阻止AO对基材的侵蚀。

关键词 ：原子氧, 侵蚀, SiO2-K2SiO3, 防护涂层

Abstract：Atomic oxygen erosion of spacecraft materials and protection by coatings were studied in the ground-based simulation facilities. The corrosion morphologies and products were characterized by several physical techniques, including scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). Silicon dioxide- potassium silicate organic-inorganic composite coatings due to higher conductivity improved resistance to high temperature and thermal cycling. The results indicated that Kapton is susceptible to AO erosion and undergoes mass loss and surface degradation. SiO2-K2SiO3 coatings have excellent properties for anti-AO effects and good stability for space environment.

Key words： Atomic Oxygen erosion SiO2-K2SiO3 organic-inorganic composite coatings

收稿日期: 2003-12-17

ZTFLH:

TG174.46

通讯作者: 严川伟 E-mail: cwyang@imr.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张蕾
	严川伟
	李绮
44.8K

引用本文:

张蕾; 严川伟; 李绮 . SiO2-K2SiO3涂层对空间材料Kaphton的防护行为研究[J]. 中国腐蚀与防护学报, 2004, 24(2): 91-94 .
Zhang Lei, Yan Chuanwei, Li Qi. PROTECTIVE EFFECTS OF SIO2-K2SIO3 ORGANIC-INORGANIC COMPOSITE COATINGS FOR THE SPACECRAFT. J Chin Soc Corr Pro, 2004, 24(2): 91-94 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I2/91

[1]RaddyMR .Effectoflowearthorbitatomicoxygenonspacecraftmaterials[J].J .Mate.Sci.,1995,30:281-307
[2]PackirisamyS ,SchwamD ,LittMH .Atomicoxygenresistantcoat ingsforlowearthorbitspacestructures[J].J.Mater.Sci.,1995,30:308-320
[3]KimKDeGroh,BanksBruceA .Atomic-oxygenundercuttingoflongdurationexposurefacilityaluminized-Kaptonmultilayerinsu lation[J].J.SpacecraftandRockets,1994,31:656-661
[4]GrossmanE ,LifshitzY ,WolanJT ,etal.InsituerosionstudyofKaptonusingnovelhyperthermaloxygenatomsource[J].J.Space craftandRockets,1999,36(1):75-78
[5]ZhangLei,YanChuanwei.StudiesontheerosionmechanismofKaptonanditsprotectiveeffect[J].Chem.J.Chin.Univ.,2003.24(6):1080-1084(张蕾,严川伟.聚酰亚胺侵蚀机理及防护效应的研究[J].高等学校化学学报,2003,24(6):1080-1084)
[6]ZhangLei,YanChuanwei,QuQing,etal.Atomicoxygenirradiationinduceddegradationofpolyimidewithoutandwithsiloxanecoating[J].Corros.Sci.Prot.Technol.,2002,14(3):78-81(张蕾,严川伟,屈庆等.原子氧对聚酰亚胺表面侵蚀及有机硅涂层保护[J].腐蚀科学与防护技术,2002,14(3):78-81)

[1]	徐涛涛, 陈祝桥, 田卫平, 王成, 朱圣龙, 王福会, 张涛, 陈明辉. ES150型纳米改性有机硅涂料的防护作用及其应用[J]. 中国腐蚀与防护学报, 2018, 38(4): 373-380.
[2]	程旭东, 孙连方, 曹志烽, 朱兴吉, 赵立新. 沿海钢筋混凝土结构Cl^-侵蚀数值模拟方法研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 144-150.
[3]	刘彤, 张艳飞, 陈旭, 王丹, 陈宇, 王冠夫. SRB对X70钢在土壤模拟溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2014, 34(2): 112-118.
[4]	蔡健平,刘明,安英辉. 铝合金防护涂层老化动力学研究[J]. 中国腐蚀与防护学报, 2012, 32(3): 256-261.
[5]	李靖,马志瀛,黄绍平,李建明,许利战. 400 Hz低压阻性小电流电弧对银石墨触头材料的侵蚀研究[J]. 中国腐蚀与防护学报, 2010, 30(3): 231-235.
[6]	王蕾胡道春. C/C复合材料抗电弧侵蚀性能研究[J]. 中国腐蚀与防护学报, 2009, 29(3): 235-240.
[7]	胡道春孙乐民上官宝. 动载荷条件下紫铜/铬青铜受流摩擦磨损性能[J]. 中国腐蚀与防护学报, 2009, 29(1): 35-39.
[8]	陈群志; 孙祚东; 陆维忠; 韩恩厚; 常铁军; 李京 . SEBF/SLF重腐蚀防护涂层应用于典型飞机结构中防腐性能综合评定[J]. 中国腐蚀与防护学报, 2005, 25(6): 365-368 .
[9]	高小建; 马保国; 赵志曼 . 西部地区水工混凝土长期腐蚀产物与腐蚀机理[J]. 中国腐蚀与防护学报, 2005, 25(5): 299-302 .

Viewed

Full text

Abstract

Cited

Shared

Discussed