中国腐蚀与防护学报  2003, Vol. 23 Issue (4): 234-238     
  研究报告 本期目录 | 过刊浏览 |
锡锌钎料的腐蚀行为研究
夏志东;穆楠;史耀武
北京工业大学材料学院
CORROSION BEHAVIOR OF TIN-ZINC BASED ALLOY SOLDER
Zhidong Xia;Nan Mu;Yaowu Shi
北京工业大学材料学院
全文: PDF(223 KB)  
摘要: 在传统的SnZn共晶钎料中加入微量稀土元素获得含稀土的Sn ZnRE钎料.采用失重法、扫描电镜腐蚀形貌观察及电化学分析技术对钎料在不同环境下的腐 蚀行为进行分析,研究SnZn系钎料的抗腐蚀性能,并与SnPb钎料进行了比较.
关键词 无铅钎料锡锌钎料锡铅钎料腐蚀    
Abstract:Environmental concerns drive market to find environ ment-friendly solder to replace the lead-bearing solder for microelectronic join ing.In this paper,the corrosion behavior of Sn-37Pb and SnZn based lead-free sol ders(including Sn-9Zn,Sn-9Zn-0.25RE) has been investigated.Mass loss evaluati on,observation of corrosion morphology by scanning electron microscope(SEM) and electrochemical testing has been conducted on.The corrosion experiments were un dertaken in tap water(room temperature),tap water(70℃),in air with high humid ity at high temperature(70℃) and in 3% NaCl solution at room temperature separ ately.The results reveal that:SnPb solder was corroded uniformly under the all c orrosion conditions mentioned in the paper.The corrosion products are likely to peeling off from the matrix for their weak joining.SnZn based solder is characte ristics with chosen corrosion of zinc for the low standard potential of zinc,res ulting in pitting of the alloy.The corrosion mechanism of this zinc-bearing sold er is a mixing of pitting and entire corrosion,leading to fast corrosion rate.Mi nimal rare-earth elements in SnZnRE solder improve the compactness of the micros tructure of SnZn alloy and its corrosion products,resulting in the slow corrosio n rate and stronger corrosion-resistance of SnZnRE solder.Based on the above exp eriments,Sn-Zn based solder will be expected to replace the SnPb solder when its competitive properties meet the required touchstones.
Key wordslead-free solder    SnZn based solder    SnPb solder    corrosi on behavior
收稿日期: 2001-11-08     
ZTFLH:  TG178  
通讯作者: 夏志东   
Corresponding author: Zhidong Xia   

引用本文:

夏志东; 穆楠; 史耀武 . 锡锌钎料的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2003, 23(4): 234-238 .
Zhidong Xia, Nan Mu, Yaowu Shi. CORROSION BEHAVIOR OF TIN-ZINC BASED ALLOY SOLDER. J Chin Soc Corr Pro, 2003, 23(4): 234-238 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2003/V23/I4/234

[1]DaleCHNevison.CorrosionofZincinMetalHandbook(Vol.13,Corrosion)[M].MetalsPark,OH :ASMInternational,1987,755-769
[2]ShiLin.AlloyThermo-Mechanism[M ].Beijing:MechanicalIn dustrialPress,1992:543-598(石霖.合金热力学[M ].北京:机械工业出版社,1992:543-598)
[3]ChungSC ,ChengJR ,ChiouSD ,ShihHC .EISbehaviorofan odizedzincinchlorideenvironments[J].Corros.Sci.,2000,42:1249-1268
[4]Bech-NielsenG ,AnneDJuhl.Corrosionmeasurementsbytitra tion(CMT ):Copper,Sn-Znalloyandaluminium[J].Corros.Sci.,1993,34(5):785-796
[5]OdnevallI,LeygrafC .TheformationofZn4Cl2(OH)4SO4·5H2Oinanurbanandanindustrialatmosphere[J].Corros.Sci.,1994,36(9):1551-1567
[6]MendozaAntonioR ,FranciscoCorvo.Outdoorandindooratmo sphericcorrosionofnon-ferrousmetals[J].Corros.Sci.,2000,42:1123-1147
[7]SabbarA ,HajjajiSEI ,BachirABen,Alaoui-EIBelghitiM ,ArinehA .EvaluationofcorrosionbehaviorofanewclassofPb-freesoldermaterials(Sn-In-Zn)[J].MaterialsandCorrosion,2001,52:298-301
[8]SzirakiL ,CsontosH ,VarsanyiML ,KissL .Corrosionmechanismoftin-zincalloysinneutralmedium[J].Corros.Sci.,1993,35(Nos1-4):371-376
[9]ZhuRizhang.MetalsCorrosion[M ].Beijing:MetallurgicalIndustri alPress,1989(朱日彰等.金属腐蚀学[M ].北京:冶金工业出版社,1989)
[10]RenKan.HandbookofMetalCorrosion[M ].Shanghai:ShanghaiScienceandTechnologyPress,1987(任侃.金属腐蚀手册[M ].上海:上海科学技术出版社,1987)
[11]SongRenying,WangXinjie,JiangShen,SongZhigang,SunLiqiang,ZhaoSuqi.Effectofrareearthelementonzinc-alloy[J].ChineseRareEarthActa,1995,13(7):479-483(宋人英,王兴杰,姜深,宋志刚,孙力蔷,赵素琦.稀土在锌合金中的作用[J].中国稀土学报,1995,13(7):479-483)
[1] 席艳君; 贺连龙; 王福会 . 纳米化对Ti48Al8Cr2Ag合金抗氧化和抗腐蚀[J]. 中国腐蚀与防护学报, 2005, 25(3): 135-141 .
[2] 胡津; 孔海宽; 徐丽新 . 时效对SiCw/2024Al复合材料应力腐蚀开裂行为的影响[J]. 中国腐蚀与防护学报, 2003, 23(6): 359-361 .
[3] 耿树江; 朱圣龙; 王福会 . 纯Ni在600℃~700℃固态NaCl和水蒸气综合作用下的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(5): 262-265 .
[4] 李容; 苟兴龙; 何晓英 . N80#钢在含H2SO3酸性溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(5): 271-275 .
[5] 于辉; 吴建华; 钱建华 . 一种海水缓蚀剂缓蚀行为的研究[J]. 中国腐蚀与防护学报, 2003, 23(5): 295-298 .
[6] 耿树江; 朱圣龙; 王福会 . 在600℃~700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(4): 193-197 .
[7] 刘大扬; 魏开金; 李文军 . 南海榆林海域环境因素对钢局部腐蚀的影响[J]. 中国腐蚀与防护学报, 2003, 23(4): 211-216 .
[8] 屈庆; 严川伟; 白玮 . NaCl在A3钢大气腐蚀中的作用[J]. 中国腐蚀与防护学报, 2003, 23(3): 160-163 .
[9] 杨怀玉; 陈家坚; 曹楚南; 曹殿珍 . H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅷ咪唑啉衍生物H2S溶液中的吸附作用行为[J]. 中国腐蚀与防护学报, 2003, 23(2): 75-78 .
[10] 刘树勋; 刘宪民; 李培杰; 吴振宁 . 高Co热作钢在AZ91D镁合金液中腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(2): 120-123 .
[11] 白宝云; 罗兴宏; 范存淦 . 奥氏体不锈钢在熔融碳酸盐中的腐蚀[J]. 中国腐蚀与防护学报, 2002, 22(5): 278-281 .
[12] 吴欣强; 敬和民; 郑玉贵 . 碳钢在高温环烷酸介质中冲刷腐蚀行为[J]. 中国腐蚀与防护学报, 2002, 22(5): 257-263 .
[13] 徐永祥; 严川伟 . 大气环境中涂层下金属的腐蚀和涂层的失效[J]. 中国腐蚀与防护学报, 2002, 22(4): 249-256 .
[14] 李远士; 牛焱; 吴维tao . 纯Cr和两种含Cr合金在ZnCl2及KCl-ZnCl2盐膜下的腐蚀[J]. 中国腐蚀与防护学报, 2002, 22(1): 27-31 .
[15] 刘烈伟; 胡倩; 郭风 . 硫化氢对不锈钢表面钝化膜破坏的研究[J]. 中国腐蚀与防护学报, 2002, 22(1): 22-26 .