离子渗金属中表层合金元素的贫化及其消除

李忠厚;刘小平;苏永安

太原工业大学;太原030024;太原工业大学;太原030024;太原工业大学;太原030024

DEPLETION OF ALLOYING ELEMENTS IN THE SURFACE LAYER PRODUCED BY DOUBLE GLOW PLASMA ALLOYING AND ITS MITIGATION

LI Zhonghou LIU Xiaoping SU Yongan (Taiyuan University of Technology; Taiyuan 030024)

全文: PDF(294 KB)

摘要: 离子渗金属中,工件表层合金贫化主要是由于离子轰击在工件表层造成一个严重的畸变层,畸变层原子具有高的扩散系数而非畸变层原子具有低的扩散系数,结果使交界区出现原子富集;同时在畸变层存在畸变梯度,这一梯度的存在支持这样的富集。离子轰击的溅射作用和溅射衰减也促使出现内层峰。提高源极电压和电流,增加单位时间内沉积到工件表面的金属原子数,或渗后进行高温扩散退火,都可以减轻和消除贫化。

关键词 ：合金贫化, 畸变梯度, 消除贫化

Abstract：In double glow plasma surface alloys, the depletion of some alloying elements in the surface layer was observed. Ion bombardment produced a seriously distorted layer beneath the sueface. The atom diffusivity in the distorted layer was higher than that in the undistorted layer. During diffusion process, the atoms gathered at interface of the distorted and undistorted layers. At the same time, the distortion gradient in the distortion zone supported this gathering. The sputtering and sputtering attenuation also promoted the generation of this inner peak of concentration. Mitigation or elimination of the depletion could be achieved by raising voltage and current of source plate, increasing metal atoms deposited on workpiece in unit time and carrying out high temperature diffusion after the plasma alloying.

Key words： Depletion of alloying element Gradient of distortion Elimination of depletion

收稿日期: 1997-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李忠厚
	刘小平
	苏永安
44.8K

引用本文:

李忠厚;刘小平;苏永安. 离子渗金属中表层合金元素的贫化及其消除[J]. 中国腐蚀与防护学报, 1997, 17(4): 295-298.
. DEPLETION OF ALLOYING ELEMENTS IN THE SURFACE LAYER PRODUCED BY DOUBLE GLOW PLASMA ALLOYING AND ITS MITIGATION. J Chin Soc Corr Pro, 1997, 17(4): 295-298.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1997/V17/I4/295

1 Murch G E, Nowick A S. Diffusion in crystalline solids, Orlande: Academic Press, Inc., 1984
2 肖纪美.合金相与相变,北京:冶金工业出版社,1987, p.183

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed