磁场和CI~-对铁在中性Na_2SO_4溶液中阳极极化行为的影响

吕战鹏;陈俊明

中国科学院上海冶金研究所;上海200050;中国科学院上海冶金研究所;上海200050

EFFECT OF MAGNETIC FIELD AND Cl~- ON ANODIC POLARIZATION BEHAVIOR OF IRON IN NEUTRAL 0.5mol/LNa_2SO_4 SOLUTION

LU Zhanpeng CHEN Junming (Shanghai Institute of Metallurgy; Chinese Academy of Sciences)

全文: PDF(444 KB)

摘要: 用动电位扫描法研究了外加磁场及Cl~-对铁在中性0.5mol/LNa_2SO_4溶液中阳极极化行为的影响。结果表明:有、无磁场下铁在含Cl~-的Na_2SO_4溶液中的阳极极化曲线都呈现活化-钝化-过钝化特征,虽然Cl~-会阻碍钝化膜的形成过程;外加磁场使E_p和E_F正移并增大i_(max)和i_(min),使钝化区范围缩小。Cl~-与磁场同时存在时对钝化膜的破坏有协同作用。

关键词 ： Fe/Na_2SO_4腐蚀, 磁场作用, Cl~-作用

Abstract：The effect of magnetic feild and Cl- on anodic polarization behavior of iron in neutral 0.5mol/L Na2so4 solution was studied using potentiodynamic method. It was shown that iron in Na2SO4+Cl-solution exhibited active- passive-transpassive characteristics in the presence or absence of magnetic field, although Cl- in the solution would hinder the formation of passive layer. The applied magnetic field would cause shift of passivation potential Ep and flade potential EF towards noble direction, increase the critical current density for passivation imax and the passive current density imin, and narrow the passive region. A synergistic effect of imposed magnetic field and Cl- on breakdown of the passive layer was reported.

Key words： Fe/Na2SO4 corrosion Effect of magnetic field Effect of Cl-

收稿日期: 1997-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吕战鹏
	陈俊明
44.8K

引用本文:

吕战鹏;陈俊明. 磁场和CI~-对铁在中性Na_2SO_4溶液中阳极极化行为的影响[J]. 中国腐蚀与防护学报, 1997, 17(1): 25-30.
. EFFECT OF MAGNETIC FIELD AND Cl~- ON ANODIC POLARIZATION BEHAVIOR OF IRON IN NEUTRAL 0.5mol/LNa_2SO_4 SOLUTION. J Chin Soc Corr Pro, 1997, 17(1): 25-30.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1997/V17/I1/25

1 Ghabashy M A. Anti-Corrosion, 1988, 35(1): 12
2 吕战鹏,陈俊明.中国腐蚀与防护学报,1996, 16(2): 115
3 Bockris J O'M, Drazic O, Despric A R. Electrochimica Acta, 1961, 4:325
4 Epelboin I, Keddam M. Electrochimica Acta, 1972, 17:177
5 Brusic V. In: Brubaker G R, Phipps P. ed. Corrosion Chemistry, Washington, D. C.: ACS,1979. Ch.6
6 Lorentz W J. Corros. Sci., 1965, 5:121
7 Evans U R. The Corrosion and Oxidation of Metals. London, Edward Arnold Ltd. 1960, p230
8 宋光铃,曹楚南,高卫红,李瑛,陈慎豪.中国腐蚀与防护学报,1994, 14(3): 175
9 曹楚南,王佳,林海潮.中国腐蚀与防护学报,1989, 9(4): 261
10 Aaboubi O, Chopart J P, Donglade J, Olivier A, etal. J Electrochem. Soc., 1990, 137:1796

[1]	吕战鹏; 杨武; 黄德伦 . 磁场对铜在含三价铁离子硫酸溶液中的腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2001, 21(3): 129-136 .

Viewed

Full text

Abstract

Cited

Shared

Discussed