聚脲聚氨酯环氧涂料用於混凝土钢筋防腐蚀的研究

林薇薇

浙江大学高分子系

A STUDY ON POLYUREA／POLYURETHANE－MODIFIED EPOXY COATING FOR CORROSION PROTECTION OF STEEL IN CONCRETE

Lin Weiwei

全文: PDF(301 KB)

摘要: 聚脲聚氨酯环氧涂料用於混凝土钢筋防腐蚀的研究林薇薇（浙江大学高分子系杭州３１００２７）钢筋混凝土建筑物耐久性下降的主要原因之一是增强钢筋的腐蚀。因为混凝土是多孔性凝胶体，空气中的氧、湿气和其它腐蚀介质能通过孔隙和细裂缝侵蚀钢筋，而钢筋变成铁锈时体积要增大２～４倍，结果产生内应力，使混凝土开裂，又进一步加剧腐蚀，造成钢筋混凝土构件破损失效。为此，目前已采用一些方法来减缓钢筋的腐蚀速度［１］。钢?...

Abstract：In order to improve corrosion prevention performance of epoxy coating，a new polyurea/polyurethane(ATPU)－modified epoxy coating was synthesized．The changes of bonding strength to steel plate were examined after immersion in corrosives such as water，alkali，salt and organic solvents etc．Results showed that this modified epoxy coating possessed excellent bonding strength and chemical resistance．Accderated electrocheimcal measurements of the modified epoxy coated steel bar embedded in concrete also proved that the ATPUepoxy coating was significantly superior to the conventional polyamide epoxy coating in corrosion prevention.

收稿日期: 1996-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	林薇薇
44.8K

引用本文:

林薇薇. 聚脲聚氨酯环氧涂料用於混凝土钢筋防腐蚀的研究[J]. 中国腐蚀与防护学报, 1996, 16(1): 69-72.
. A STUDY ON POLYUREA／POLYURETHANE－MODIFIED EPOXY COATING FOR CORROSION PROTECTION OF STEEL IN CONCRETE. J Chin Soc Corr Pro, 1996, 16(1): 69-72.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1996/V16/I1/69

1SwamyRN．CorrosionandCorrosionProtectionofSteelinConcrete,England:SheffildAcadermicPress,19942林薇薇,沈烈．中国粘合剂,1992,1(5):303KurdeyAE．Anti-Corrosion1992,July:24SwarajP．SurfanceCoating,NewYork:Johnwiley&SonnsLtl,1985．2615MansfeldF．CorrosionMechanisms;BerkelyCalifornia:HenhzHeinemmonnInc,1989．119

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed