氢蚀程度对20G钢K_(IC)及△K_(th)的影响

中国腐蚀与防护学报

1995, Vol. 15

Issue (4): 308-312

研究报告

本期目录 | 过刊浏览

氢蚀程度对20G钢K_(IC)及△K_(th)的影响

郦建立;李晓刚;谢根栓;李彦;姚治铭;李劲;柯伟

中国科学院金属腐蚀与防护研究所腐蚀与防护国家重点实验室;抚顺石油学院;抚顺石油三厂

FRACTURE TOUGHNESS AND FATIGUE THRSSHOLD FOR 20G STEEL AFTER HYDROGEN ATTACK

Li Jianli;Li Xiaogang; Xie Gensuan; Li Yan; Yao Zhiming;Li Jin; Ke Wei(Corrosion Science Labolatory; Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences;Shengyang)(Fushun Petroleum Institute)(The Third Retinery of Fushun)

全文: PDF(1290 KB)

摘要: 氢蚀程度对２０Ｇ钢Ｋ_（ＩＣ）及△Ｋ_（ｔｈ）的影响郦建立，李晓刚，谢根栓，李彦，姚治铭，李劲，柯伟（中国科学院金属腐蚀与防护研究所腐蚀与防护国家重点实验室沈阳１１００１５）（抚顺石油学院，抚顺石油三厂）１引言氢腐蚀（ＨＡ）使材料的力学性能和疲劳断裂性能严重恶化，是化学工业、石油化工、煤转化工业临氨装置主要的损坏形式。对临氢后的２．２５Ｃｒ－ＩＭｏ＄疲劳性能、断裂性能的研究结果表明，氢蚀使西Ｋ?...

Abstract：The effects of hydrogen atted (HA) caused by exposure to hydrogen atmosphere at different temperstures under 18MPa for 240hrs on mechanical Properties for 20G steel were studied. In this study hydrogen attack intensity was defined as % of strength loss. The tensile tests showed that tensile strength decreased considerably with increasing hydrogen attack. The COD testing indicated that δc,KIC decreased with increasing hydrogen attack. The variation of threshold △K value with hydrogen attack was not so simple.It decreased initially and then increased, resulting in a valley on △K～HA % plot. It was suggested thst the knowledge of influence of HA % on △Kth and KIC would be important for engineering practice.

收稿日期: 1995-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	郦建立
	李晓刚
	谢根栓
	李彦
	姚治铭
	李劲
	柯伟
44.8K

引用本文:

郦建立;李晓刚;谢根栓;李彦;姚治铭;李劲;柯伟. 氢蚀程度对20G钢K_(IC)及△K_(th)的影响[J]. 中国腐蚀与防护学报, 1995, 15(4): 308-312.
. FRACTURE TOUGHNESS AND FATIGUE THRSSHOLD FOR 20G STEEL AFTER HYDROGEN ATTACK. J Chin Soc Corr Pro, 1995, 15(4): 308-312.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1995/V15/I4/308

1王牧．金属学报增刊Ⅱ1984,24:2602抚顺石油三厂．“5#反应器解剖试验”,1987．93蒋家羚,张勤．机械强度,1988,10(4):764陈南平,顾守仁,沈万慈．脆断失较分析,清华大学出版社,1993．95胡传忻,断裂力学及其工程应用,北京工业大学出版社,19896李忠超．第六届全国疲劳学术会议论文集,1993．87SteuberRJ,GeigerGH．MetallTrans,1983,14A:9638余宗森．钢的高温高压氢腐蚀,化学工业出版社,1987．119郦建立,李晓刚,谢根柱,姚治铭,李劲,何伟.金属学报,1995,(1):B26

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed