Ti-24Al-11Nb金属间化合物的氢致滞后开裂

张跃;王忆;王燕斌;褚武扬;肖纪美

北京科技大学

HYDROGEN INDUCED DELAYED CRACKING OF INTERMETALLIC COMPOUND Ti-24Al-11Nb

Zhang Yue; Wang Yi; Wang Yanbin; Chu Wuyan; Xiao Jimei(University of Science and Technology; Beijing)

全文: PDF(3506 KB)

摘要: Ｔｉ－２４Ａｌ－１１Ｎｂ金属间化合物的氢致滞后开裂张跃，王忆，王燕斌，褚武扬，肖纪美（北京科技大学北京１０００８３）１引言复相金属间化合物Ｔｉ－２４ＡＬｌｌＮｂ合金是一种重要的新型高温结构材料，已被美国宇航局用作为新一代宇航飞机的发动机材料及结构件．鉴于许多金属间化合物都表现出较强的氢脆敏感性［１－５］，因而有必要研究该合金在室温条件下的氢致开裂性能及其与组织结构的关系．本工作采用单边缺口试?...

Abstract：The behavior of hydrogen induced delayed cracking(HIDC) of intermetallic compound Ti-24Al-11Nb was investigated with single-edge notched specimens under cathodic charging. It was found that HIDC could occur for all specimens with three different kinds of heat treatment. The threshold values KIH/Kic were 0.43, 0.59 and 0.85 respectively, for specimens solution if eated (ST) at 1000 ℃ and air coooled (KIc=20MPam1/2), those ST at 1150 ℃ and furnace cooled (FC) (KIc=18.4MPam1/2) and those ST at 1000 ℃ FC (KI.=15.7MPam1/2).The experiments also showed that the HIDC of the alloy was induced by atomic hydrogen and not by hydrides. The fractograph of HIDC was dependent on the KI value. Then KI approached KIH, dimples were observed on the fracture surface; when KI became higher, the fractograph of HIDC was cleavage-like,similar to that of overloaded fracture.

收稿日期: 1994-04-25

基金资助:国家自然科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张跃
	王忆
	王燕斌
	褚武扬
	肖纪美
44.8K

引用本文:

张跃;王忆;王燕斌;褚武扬;肖纪美. Ti-24Al-11Nb金属间化合物的氢致滞后开裂[J]. 中国腐蚀与防护学报, 1994, 14(2): 143-150.
. HYDROGEN INDUCED DELAYED CRACKING OF INTERMETALLIC COMPOUND Ti-24Al-11Nb. J Chin Soc Corr Pro, 1994, 14(2): 143-150.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1994/V14/I2/143

1StoloffNS．In:HydrogenEffectsonMaterialBehavior,EditedbyMoodyNR,ThompsonAW．TheMinerals,MetalsandMaterialsSociety,1990,p4832ZhangDZ,ChuWY,HaialJM．Scripta．Metal．Mater,1992,26:273ChuWY,ThompsonAW,WilliamsJC．ActaMetal．Mater,1992;40:4554ChuWY,ThompsonAW．MetallTrans．A,1992,23A:12995褚武扬,肖纪美,ThompsonAW．ActaMetall．Sinica,1992,5A:2866褚武扬．氢损伤与滞后断裂,北京:冶金出版社,1988,4867ChuWY,ThompsonAW．MetallTrans．A,1991,22A:718ChuWY,ThomponAW．In:HighPerformanceCompositesforthe1990's,EditedbyDasSK,BallardCP,MarikarF．TMS,143

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed