钇对Fe-Cr-Al合金在纯SO_2气氛中高温腐蚀行为的影响

曹铁梁;潘辉英;董荷花;张允书

中国科学院上海冶金研究所;中国科学院上海冶金研究所;中国科学院上海冶金研究所;中国科学院上海冶金研究所

THE EFFECT OF YTTRIUM ON HIGH TEM PERATURE CORROSION BEHAVIOR OF Fe-Cr-Al ALLOYS IN PURE SO_2 GAS ATMOSPHERE

Cao Tieliang; Pan Huiying; Dong Hehua and Zhang Yunshu ( Shanghai Institute of Metallurgy; Chinese Academy of Sciences)

全文: PDF(2136 KB)

摘要: 研究了Fe-20Cr-5Al和Fe-20Cr-5Al-0.5Y合金在1200℃,1atm纯SO_2气氛中的高温腐蚀行为。测定了腐蚀动力学曲线,观察了腐蚀产物表面,横截面和脆断断口的形貌,并分析了元素的分布,确定了腐蚀产物的相组成。结果表明,这两种合金在300小时实验周期内只发生氧化反应,没有遭受硫化腐蚀。无丫合金表面发展出双层结种氧化膜,而钇的添加使合金表面氧化膜呈单层结构,且粘着性显著改善。钇的有益作用在于对Al~(3+)在α-Al_2O_3中扩散的有效抑制作用。

Abstract：High temperature corrosion behavior of Fe-20Cr-5Al and Fe-20Cr-5Al-0.5Y alloys in pure SO_2 atmosphere at 1200℃ was studied. The corrosion kinetics of these alloys was measured. X-ray diffraction was employed to identify the components in corrosion products. The morphologies of corrosion product surfaces, cross sections and fractures were examined by means of SEM, and the element distribution in corrosion product scales was also analyzed. The experimental results show that the alloys underwent pure oxidation without sulfidation observed in the experimental condition during the period of time of 300 hours. A duplex oxide scale was developed on the surface of the yttrium-free alloy while a single layer oxide scale was produced for the yttrium-containing alloy. The adhesion of the oxide scale was found to be remarkably improved by the addition of yttrium in the alloy. The beneficial effect of yttrium is discussed and attributed to the effective blocking of the bulk diffusion of Al~(3+)in the Al_2O_3 scale in the presence of yttrium.

收稿日期: 1992-04-25

基金资助:中国科学院腐蚀科学开放研究实验室课题的一部分

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曹铁梁
	潘辉英
	董荷花
	张允书
44.8K

引用本文:

曹铁梁;潘辉英;董荷花;张允书. 钇对Fe-Cr-Al合金在纯SO_2气氛中高温腐蚀行为的影响[J]. 中国腐蚀与防护学报, 1992, 12(2): 116-124.
. THE EFFECT OF YTTRIUM ON HIGH TEM PERATURE CORROSION BEHAVIOR OF Fe-Cr-Al ALLOYS IN PURE SO_2 GAS ATMOSPHERE. J Chin Soc Corr Pro, 1992, 12(2): 116-124.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1992/V12/I2/116

[1] Reed. D. J. and Wuensch, B. J., J. Amer. Ceram. Soc., 63, 88(1980)
[2] Oishi, Y. and Kingery, W. D., J. Chem. Phys, 33 480(1960)
[3] Paladino, A. E. and Kingery. W. D., ibid., 37, 957(1962)
[4] Wood, G. C. and Scott, F. H., in "High Temperature Corrosion", NACE-6, Rapp, R. A., Ed., P227, NACE, Houston,(1983)
[5] Pappis, J, and Kingery, W. d., J, Amer, Ceram, Soc., 44, 459(1961)
[6] EI-Alat, M. M. and Kroger, F. A., ibid., 65, 280(1982)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed