应力对腐蚀裂缝内闭塞区腐蚀行为的影响

左景伊;刘幼平;许淳淳

北京化工学院;北京化工学院;北京化工学院

EFEFCTS OF STRESS ON THE CORROSION BEHAVIOUR OF OCCLUDED CELL INSIDE S.C.CRACKS

Zuo Jingyi Liu Youping Xu Chunchun(Beijing Institute of Chemical Technology)

全文: PDF(941 KB)

摘要: 摘要采用模拟“I 8—8不锈钢/c卜”体系腐蚀裂缝形成过程不同阶段的闭塞区溶液.以电化学方法研究了1.8—8不锈钢加载到屈服后在这些溶液中的腐蚀行为。结粜表明:当溶液pH值低于一临界值(约】.8)后受力试样的腐蚀开始加速.而不受力试样加速腐蚀的临界pH值则较低.约为1.5。低于临界值,受力与未受力试样的商蚀电位都从约一200mY.SCE(位于钝化区)突然下降到一400mY左右(处于活化区).表明钝化膜完全破裂。受力屈服后合金的钝化能力变差。将上述闭塞区溶液中测得的动电位极化曲线上的特征电位.电位一时间曲线上所得到的稳定开路电位.放氢平衡线和免蚀线.以及闭塞区腐蚀和放氢动力学曲线等叠加绘制而成的实验电位一pH图,能解释应力腐蚀裂缝内的热力学和动力学行为。

Abstract：For the 18-8 stainless steel/Cl~- system,polarization scans and linear polarization tests were performed with specimens stressed above yield point and stress free in simulated occluded solutions of different pH and Cl~- concentration representing the chemical condi- tions of different stages in occluded corrosion cell.The results showed that the corrosion of stressed specimens started to accelerate below a critical pH value of about 1.8 at 90℃. while the stress free specimens had a critical pH value about 1.5.The passivating effect al- so decreased for stressed alloy.The open-circuit potentials of both stressed and sterss free specimens dropped suddenly from about-200mV(SCE) in passive region to-400mV (SCE) in active region when pH decreased below the critical value,indicating that the pas- sive film had been ruptured completely.The potential/pH diagrams were constructed by superimposing the above potentiodynamic polarization curves,potential/time curves,and the hydrogen equilibrium curves and immunity border lines which were determined experi- mentally in simulated OC solutions.The potential/pH diagrams interpreted the thermody- namic as well as kinetic behaviour inside stressed cracks.

收稿日期: 1991-02-25

基金资助:国家自然科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	左景伊
	刘幼平
	许淳淳
44.8K

引用本文:

左景伊;刘幼平;许淳淳. 应力对腐蚀裂缝内闭塞区腐蚀行为的影响[J]. 中国腐蚀与防护学报, 1991, 11(1): 55-66.
. EFEFCTS OF STRESS ON THE CORROSION BEHAVIOUR OF OCCLUDED CELL INSIDE S.C.CRACKS. J Chin Soc Corr Pro, 1991, 11(1): 55-66.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1991/V11/I1/55

[1] Zuo.J.:Jin,Z.:Sun,R.;Xu.Y.,Feng,X..Corrosion.44,539(1988)
[2] Fontana.M.G.;Greene.N.D.《腐蚀工程》左景伊译.化学工业出版社,1982年,P39～41
[3] Pourbaix.M..Localized Corrosion,Staehle.R.W.et al Ed..NACE.Houston,Tex.1974年,P12
[4] Brown.B.F.;Fujii,C.T.:Dalberg,E.P..J.Electrochem.Soc..116,218～219(1969)
[5] Rosenfeld,L.:Marshakov.I.K.,Corrosion,20,115t(1964)
[6] Zuo,J.:Gu,B.;Liu,Y.,“Effects of Stress on Cracking Velocity and Critical pH Value inside S.C.Cracks”.Corrosion, 47(3) ,(1991)
[7] Zuo.J.:Pourbaix.M.:Xu.C.:liu.Y.,Corrosion Science.29,557～566(1989)
[8] Zuo.J.;Jin,Z.,Proc. 9th ICMC.Toronto,Canada.4,336～343(1984)
[9] 《金属腐蚀及其保护的理论》.华保定等译.中国工业出版社.1964年.P104

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed