喷涂锌、铝对921船用高强钢应力腐蚀断裂的影响

中国腐蚀与防护学报

1990, Vol. 10

Issue (1): 79-84

研究报告

本期目录 | 过刊浏览

喷涂锌、铝对921船用高强钢应力腐蚀断裂的影响

章岳;王体权;俞宏英

武汉材料保护研究所;武汉材料保护研究所;武汉材料保护研究所

EFFECT OF THERMAL-SPRAYED ZINC AND ALUMINIUM ON THE STRESS CORROSION CRACKING OF 921 HIGH-STRENGTH STEEL FOR SHIP BUILDING

Zhang Yue Wang Tiquan Yu Hongying (Wuhan Research Institute of Material Protection)

全文: PDF(1308 KB)

摘要: <正> 由于高强度钢在水介质中有较强的环境敏感断裂倾向,在海水中能否用锌、铝等阳极性金属涂层进行防护就成为防腐蚀工作者十分关心的问题。现已发现在高强度钢螺拴上无论是电镀锌还是热浸镀锌都增加基材的氧致应力腐蚀断裂敏感性。从而,人们考虑在高强钢构件上用铝保护涂层。最近有在海洋钻井平台的高强钢柱脚和立管上使用喷涂铝层保护的报道。本工作采用锌、铝片与试样偶合或外加恒电位的方法,研究921船用高强度钢在锌、

Abstract：The effect of thermal-sprayed zinc(TSZ)and aluminium(TSA) on stress corrosion cracking susceptibility of 921 high-strength steel in seawater was studied by slow strain rate technique,with the porosity and local peeling of TSZ or TSA simulated,The test results showed that the potential of the steel coupled to zinc(about-1040mV, SCE)was in the potential range of remarkable hydrogen embrittlem- ent(HE)of the steel in artificial seawater.It would be very dang- erous to have TSZ applied on 921 steel as it might cause HE of the latter.On the other hand,the potential of the steel coupled to alum- inium(about-800mV,SCE)is in the safe and usable range with TSA providing good cathodic protection to the stressed steel component,

收稿日期: 1990-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	章岳
	王体权
	俞宏英
44.8K

引用本文:

章岳;王体权;俞宏英. 喷涂锌、铝对921船用高强钢应力腐蚀断裂的影响[J]. 中国腐蚀与防护学报, 1990, 10(1): 79-84.
. EFFECT OF THERMAL-SPRAYED ZINC AND ALUMINIUM ON THE STRESS CORROSION CRACKING OF 921 HIGH-STRENGTH STEEL FOR SHIP BUILDING. J Chin Soc Corr Pro, 1990, 10(1): 79-84.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1990/V10/I1/79

[1] 李仁顺,航天工艺,哈尔滨工业学校,30(1983)
[2] Townsend,H.E.Jr,Hydrogen in Metals,Proc.of an Int.Conf.on the Effects of Hydrogen on Materials Properties and Selection and Structural Design,223(1973)
[3] Salama,M.H.;Thomason W.H.,J.Petrol Technol.,1913(1984)
[4] Cooper,M.T.,.Jr;Vardon D.C.,Offshore Technol.Conf.,Paper,No.4972,Houston,TX,(1985)
[5] 曹楚南,腐蚀试验数据的统计分析,化学工业出版社,1988年,P39
[6] Syrett,B.C.,Corrosion,27(7) ,270(1971)
[7] Hovla,nd,I.,Proe.of the 8th ICMC,1321(1981)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed