带镀层GC-4超高强度钢的腐蚀断裂

金石;李世杰

西北工业大学;西北工业大学

STRESS CORROSION CRACKING BEHAVIOR OF GC-4 ULTRA-HIGH STRENGTH STEEL WITH ELECTROPLATED COATINGS

Jin Shi and Li Sihjie (Northwestern Polytechnical University)

全文: PDF(2052 KB)

摘要: 应用慢拉伸及断裂力学方法研齐了带镀层的GC-4钢(40CrMnSiMoVA)在3.5％NaCl中的应力腐蚀特性,并与裸钢作了对比。结合扫描电镜及宏观断口分析,探讨了失效机理。研究表明,阴、阳极镀层均使钢的KIscc降低,da/dt(Ⅱ)显著增加,其影响依无氰Cd、Cd-Ti、Cr的次序增加。慢拉伸试验结果说明,阴、阳极极化均使GC-4裸钢延性降低。根据BL-WOL试样裂纹扩展在表面处较内部为快以及阴、阳极镀层、平面应变状态对断口形貌的影响,可以认为带镀层与不带镀层GC-4钢的腐蚀断裂机理为裂尖阳极溶解与氢脆共同作用,并且裂尖溶解将直接参与导致裂纹扩展.从而对高强度钢腐蚀断裂的纯氢脆机理作出修正。

Abstract：Stress corrosion cracking (SCC) behavior and failure mechanism of GC-4 steel (40CrMnSiMoVA) with electroplated coatings in 3.5% NaCl solution were investigated and compared with those of bare steel using slow-strain rate tension and fracture mechanics methods. Both micro and macro-fractographic analyses were conducted using SEM and optical microscope. It was found that both anodic and cathodic electroplated coatings decreased K_(ISCC) and increased the crack propagation rate da/dt (Ⅱ ). The extent of influence on the cracking behavior by different electroplated coatings increased in the sequence of noncyanide Cd,Cd-Ti, and Cr. The slow tensile tests showed that both anodic and cathodic polarization reduced the ductility of steel. According to the fact that the crack propagated faster on the side surface than in subsurface layer and even than in the central part of BL-WOL specimens, and according to the influences of different platings as well as the plane strain conditions on the macro-fractographic morphology of crack growth, it was suggested that the SCC mechanism of GC-4 steel with and without plating in aqueous solutions involves combined action of local anodic dissolution at the crack tip and hydrogen assisted cracking rather than hydrogen embrittlement alone. In addition, the crack tip dissolution contributed to the crack propagation directly.

收稿日期: 1989-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	金石
	李世杰
44.8K

引用本文:

金石;李世杰. 带镀层GC-4超高强度钢的腐蚀断裂[J]. 中国腐蚀与防护学报, 1989, 9(4): 297-306.
. STRESS CORROSION CRACKING BEHAVIOR OF GC-4 ULTRA-HIGH STRENGTH STEEL WITH ELECTROPLATED COATINGS. J Chin Soc Corr Pro, 1989, 9(4): 297-306.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1989/V9/I4/297

[1] Rinker, J.G: Hochman, R.; Corrosion, 28 (6) .231～232 (1972)
[2] Altura, D., Metal Finishing, 72 (9) 45～46, 50(1974)
[3] Karpenko, G.V.: Pokhmurovski, V.I., Stress Corrosion Cracking of Steels, 152～157 (1979)
[4] 秦月文等,中国腐蚀与防护学报,3(2) ,97～103(1983)
[5] 金石;刘晓坤,Corrosion Cracking, edited by Goel, V.S., ASM, Metal Park, U.S.A., 69～72 (1986)
[6] 金石;朱保华,全国第四届海水、工业水及生物腐蚀学术报告会论文集,(1987)
[7] 航空材料研究所,主起落架活塞杆裂纹攻关技术总结,(1984)
[8] 金石等,全国第二届应力腐蚀与氢脆会议论文集,(1986)
[9] Parkins, R.N., et.el.,Corrosion Science, 24 (8) 709～730 (1984)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed