P~+-B~+-Mo~+-N~+多元离子注入提高2Cr13钢耐蚀性的研究

于福洲;利福干

北京化工学院;北京化工学院

USE OF P~+-B~+-Mo~+-N~+ MULTIPLE ION IMPLANTATION TO IMPROVE CORROSION RESISTANCE OF 410 STAINLESS STEEL

Yu Fuzhou and Li Fugan (Beijing Institute of Chemical Technology)

全文: PDF(708 KB)

摘要: <正> 离子注入技术用于提高耐水溶液腐蚀的研究近年来正在蓬勃开展。研究表明,在一定的原子/基材组合和较好的注入条件下,可以在金属表面获得耐蚀性优异的非晶态层。 Moute等指出,低碳钢上注入P~+以后,使孔蚀电位提高900mV左右;胡兆民等在0Cr15钢上注入Dy~+,孔蚀电位提高400mV。美国已有成功地用于防止飞机轴承孔蚀的实

Abstract：Multiple ion implantation is used to improve the resistance of 410 stainless steel(SS)to localized corrosion. Potentiodynamic polarization curves show that the passivity of P~+-B~+ implanted 410 SS is better than that of unimplanted 304 SS in 0.1NH_2SO_4 solution at 30℃; the pitting potential(E_h=E_(10)μA/cm~2)of P~+-B~+ implanted 410 SS is about 500mV more noble than that of unimplanted 304 and 316L (urea grade)SS in 1NHAc/NaAc+0.5％/NaCl solution at 30℃. The passivity of P~+-B~+-Mo~+-N~+ implanted 410 SS is better than that of unimplanted 316L(U.G.)and 25Cr-22Ni-2Mo-N SS, and the pitting potential of P~+-B~+-Mo~+-N~+ implanted 410 SS is about 600mV more noble than that of unimplanted 316L (U. G. )and 25Cr-22Ni-2Mo-N SS, both in HAc/NaAc+0.1 NNaCl solution with pH 4 at 30℃. All those results illustrate that the multiple ion implantation improves the passivity and pitting resistance notably. This conclusion is supported by the results of corrosion weight loss test in 0.1NH_2SO_4 solution at 45℃ for72 hours and the results of pitting corrosion test in 0.1N NaCl+0.07％H_2O_2 solution at 20℃ for 24 hours. Both electron diffraction and micromorphology observation demonstrate that surface layers of 410 SS modified by multiple ion implantation are amorphous. Therefore it is thought that notable improvement of corrosion resistance of implanted 410 SS results from amorphous surface layer containing such benificial elements as Cr, Mo, N and so on.

收稿日期: 1987-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	于福洲
	利福干
44.8K

引用本文:

于福洲;利福干. P~+-B~+-Mo~+-N~+多元离子注入提高2Cr13钢耐蚀性的研究[J]. 中国腐蚀与防护学报, 1987, 7(4): 292-296.
. USE OF P~+-B~+-Mo~+-N~+ MULTIPLE ION IMPLANTATION TO IMPROVE CORROSION RESISTANCE OF 410 STAINLESS STEEL. J Chin Soc Corr Pro, 1987, 7(4): 292-296.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1987/V7/I4/292

[1] Sood, D. K.. Physics Letters, A. 68A, 469 (1978)
[2] Ali, A.; Grant, W. A.; Grundy. P. J., Philosophical Magazine B, 37, 353 (1978)
[3] Sood, D, K. Radiation Effects, 63, 141 (1982)
[4] Johnson, E., et al., J. Microscopy, 116, 77(1979)
[5] Knapp, J. A., et al., Ion Implantation Metallurgy, 152(1979)
[6] Bonora, P. L.; Cerisola, G.; Tosello, C.; Tosto, S., Ion Implantation into Metal, 35(1982)
[7] Monte. S. W.; Robert, L. C., Corrosion, 40, 307(1984)
[8] 胡兆民、刘凤英、邵统义.全国第三届电子束、离子束、光子束会议论文集(1984)
[9] Wang, Y. F., et al., AD-A097230/7。
[10] 利福干、北京化工学院硕士论文(1985)H

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed