用AES和EPMA研究Fe-Cr合金钝化膜和蚀孔内壁的组成特征

杨德钧;李方;吴荫顺;张文奇

北京钢铁学院;北京钢铁学院;北京钢铁学院;北京钢铁学院

THR AES AND EPMA STUDY OF PASSI VE FILM AND PIT SIDEWALL OF Fe--Cr ALLOYS

Yang Dejun;Li Fang;Wu Yinshuen;Zhang Wenqi Beijing University of Iron and Steel Technology

全文: PDF(1632 KB)

摘要: 采用 AES 和 EPMA 对三种 Fe-Cr 合金在3.5%NaCl 溶液中的钝化膜以及点蚀孔的内壁进行了分析,由 Ar~+溅射得到了 Cr~+/Fe 比随深度变化的分布,考察了铬在钝化膜中的作用.通过实验和分析证明:Fe-Cr 合金表面钝化膜和点蚀孔内壁的 Cr/Fe 比都明显高于基体的 Cr/Fe 比,决定钝化膜性能的重要因素是 Cr/Fe 比,并且 Cr/Fe 比越高,钝化膜的保护性越好。

Abstract：AES and EPMA have been used to study the passive film and the pit sidewall of Fe-Cr alloys which contain 13%,17% and 28%Cr in 3.5%NaCl solution.By Ar~+ sputtering,the Cr/Fe ratio versus the thickness of the passive film is obtained,and the behavior of Cr in the film has beeninves- tigated.Experiments and analyses show that the Cr/Fe ratio both in the surface passive film and in the pit sidewall of Fe-Cr alloys are markedly higher than that of base materials.The most important factor withregard to protective ability of the passive film is the Cr/Fe ratio in thefilm.The higher the Cr/Fe ratio,the better the protective ability of thefilm is.

收稿日期: 1985-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杨德钧
	李方
	吴荫顺
	张文奇
44.8K

引用本文:

杨德钧;李方;吴荫顺;张文奇. 用AES和EPMA研究Fe-Cr合金钝化膜和蚀孔内壁的组成特征[J]. 中国腐蚀与防护学报, 1985, 5(4): 284-290.
. THR AES AND EPMA STUDY OF PASSI VE FILM AND PIT SIDEWALL OF Fe--Cr ALLOYS. J Chin Soc Corr Pro, 1985, 5(4): 284-290.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1985/V5/I4/284

[1] Castle,J.E.,Clayton,C.R.,Corr.Sci.,17,7(1977)
[2] Barnes,G.J.,Alday,A.W.,Jerner,R.C.,J.Eletrochem,Soc.,119,684(1972)
[3] Hultquist,G.,Leygraf,C.,Corrosion,36,12,(1980)
[4] Palmbery,P.W.,Analytical chemistry.,45,549(1973)
[5] 林荣富等,金属学报,18,586(1982)
[6] Asami,K.,Corr.Sci.,16,909(1976)
[7] 李方,北京钢铁学院硕士研究生论文,(1984)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed