双相不锈钢耐应力腐蚀破裂机理的电化学研究

张文奇;于福洲;朱应扬

北京钢铁学院;北京钢铁学院;北京化工学院;北京钢铁学院

AN INVESTIGATION OF THE MECHANISM OF STRESS CORROSION RESISTANCE IN DUPLEX STAINLESS STEEL BY ELECTROCHEMICAL METHOD

Zhang Wenqi Yu Fuzhou Zhu Yingyang (Beijing University of Iron and Steel Technology)

全文: PDF(3383 KB)

摘要: 研究了以奥氏体为基体的和以铁素体为基体的两类双相不锈钢中第二相对应力腐蚀裂纹发展的影响,并采用选择性屏蔽某一相、测定另一相极化曲线等电化学方法探讨了这种影响的作用机理。结果表明:对应于耐应力腐蚀破裂的情况,两类双相钢中的第二相都表现出了对应力腐蚀裂纹发展的阻碍作用;同时,在电化学行为方面都起着阴极作用。因此,作者认为,第二相不易发生阳极溶解是其阻碍应力腐蚀裂纹发展,提高双相不锈钢耐应力腐蚀性能的重要原因。

Abstract：The effect of secondary phase on stress corrosion cracking propagation was studied and its mechanism was discussed according to electrochemical behavior of each phase in the duplex stainless steel with austenitic or ferritic matrix. The polarization curve of each phase was measuredin situ by a technique of shielding microstrueture selectively.It was confirmed that the secondary phase (δ-phase in austenite-basesteel or γ-phase in ferrite-basesteel)has the effect of hindering crack from propagation and it acts as a cathode under such a condition that stress corrosion cracking is hampered.Therefore the authors consider the improbable anodie dissolution of the secondary phase as one of main reasons of hindering crack propagation with aresult of increased stress corrosion resistance of the duplex stainless steel.

收稿日期: 1985-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张文奇
	于福洲
	朱应扬
44.8K

引用本文:

张文奇;于福洲;朱应扬. 双相不锈钢耐应力腐蚀破裂机理的电化学研究[J]. 中国腐蚀与防护学报, 1985, 5(1): 18-25.
. AN INVESTIGATION OF THE MECHANISM OF STRESS CORROSION RESISTANCE IN DUPLEX STAINLESS STEEL BY ELECTROCHEMICAL METHOD. J Chin Soc Corr Pro, 1985, 5(1): 18-25.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1985/V5/I1/18

[1] Edeleanu,C.,Jo Iron Steel Inst,173,140(1953)
[2] 小若正伦,长野博夫,工藤纠夫,山中和夫.防食技术,30,4． 218(1981)
[3] Shimodaira,S.,Takano.M.,Takizawa,Y.,Kamide,H.,Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys.Unieux-Fimning,1003(1973)
[4] Edeleanu,C.,Stress Corrosion Cracking and Embrittlement,Wiley New York,126(1956)
[5] Latanison,R.H.,Slaehle,R.E.,Fundamental Aspects of Stress Corrosion Cracking.NACE Houston,214(1969)
[6] Denhard,F.E.,Corrosion,16,359t(1960)
[7] 淹沢贵久男,志水康彦,米田英作,庄司戈止,田村今男,铁と钢,65,615(1979)
[8] Hochmamn,J.et al.,Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys.Unienx-Fimning,965(1973)
[9] Hinse,J.G.,Hugill,R.G.,Physical Metallurgy of Stress Corrosion Fracture,Interscience,New York(1959)
[10] Nielsen,N.A.,Corrosion,20,105t(1964)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed