稳定奥氏体不锈钢的氢脆

中国腐蚀与防护学报

1984, Vol. 4

Issue (3): 213-217

研究报告

本期目录 | 过刊浏览

稳定奥氏体不锈钢的氢脆

高学镕;李继森;刘沃恒

机械工业部合肥通用机械研究所;包头冶金研究所;包头冶金研究所

HYDROGEN EMBRITTLEMENT OF STABLE AUSTENITIC STAINLESS STEEL

Kao Xuerong (Hefei Institute of General Machinery; MMB) Li Jisen Liu Woheng (Baotou Research Institute of metallurgy)

全文: PDF(2439 KB)

摘要: 用光学显微镜,扫描电镜和X射线衍射仪研究了稳定的奥氏体不锈钢的氢脆现象。结果表明:1.阴极充氢能引起试样表面γ→ε转变,并有新的f_(cc)相的出现。2.充氢可使试样表面形成裂纹。3.拉伸试样表面充氢层的断口是穿晶解理断口。断口中的二次裂纹是沿着滑移线的。上述结果证明:α′马氏体转变对于奥氏体钢的氢脆并不是必要的条件。稳定的奥氏体不锈钢中也会发生氢脆现象。

Abstract：Hydrogen embrittlement of stable austenitic stainless steel Cr20Ni25 has been investigated. Crack formation and phase transformation on the surface of the specimens have been observed. It is shown that electrolytic hydrogen charging promotes the transformation of e-martensite on the surface of specimens, the formation of surface crack and the formation of new fcc phase. Transgranular cleavage fracture is shown for the charged layer in tensile specimen. The crack propagates along slip face.The present study suggests that stable austenitic stainless steel is also subject to hydrogen embrittlemt. The transformation of α′-martensite may be not necessary for hydrogen embrittlement of austenitie stainless steel.

收稿日期: 1984-06-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	高学镕
	李继森
	刘沃恒
44.8K

引用本文:

高学镕;李继森;刘沃恒. 稳定奥氏体不锈钢的氢脆[J]. 中国腐蚀与防护学报, 1984, 4(3): 213-217.
. HYDROGEN EMBRITTLEMENT OF STABLE AUSTENITIC STAINLESS STEEL. J Chin Soc Corr Pro, 1984, 4(3): 213-217.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1984/V4/I3/213

[1] Whitemen, M. B.; Troian, A. R., Corrosion, 21, 53(1965)
[2] Vaugham, D. A., Corrosion, 19, 315t, (1963)
[3] Benson, R. B. Jr., Trans. Met. Soc., AIME, 242, 2199(1968)
[4] 交通大学,《金属断口分析》,国防工业出版社,159(1979)
[5] Eliezer, D.; Chakrapani, D. G.; Altsletter, C. J.; Pugh, E. N., Met. Trans., V. 10A, (7) , 935(1979)
[6] Hanninen, H.; Hakkarainen, T., Met. Trans., 10A, 1196(1979)
[7] Holzworth, M. L.; Louthan, M. R. Jr., Corrosion, 24, 110(1968)
[8] 蒲地一义,宫田节夫,日本金属学会志,33,824(1969)
[9] 羽本秀树,浅野滋,大塚陆郎,日本金属学会志,40,(8) ,796(1976)
[10] 蒲地一义,峠睦,日本金属学会志,40,(8) ,821(1976)
[11] Hideya Okada, Corrosion, 26, 183(1970)
[12] Langc, K. W., "Hydrogen in Metals" Proceeding of the 2nd International Congress, V. 1A5, (1977)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed