一种新型奥氏体Fe-Mn-Al耐热钢铝化物涂层相变的研究
管恒荣;黄有山;楼翰一;白林祥
中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所
AN INVESTIGATION OF PHASE TRANSFORMATION IN ALUMINIDE COATING OF A NEW AUSTENITIC Fe—Mn—Al HEAT—RESISTING STEEL
Guan Hengrong Huang Youshan Lou Hanyi and Bai Linxiang (Institute of Metal Research; Chinese Academy of Sciences)
全文: PDF(765 KB)  
摘要: 对一种新型奥氏体Fe—Mn—Al耐热钢铝化物涂层的显微结构、组成、相变进行了详细地研究。渗层共分两层,外层为有序超结构固溶体FeAl,内层由FeAl、β-Mn,V_4C_3组成。当这种涂层在静态空气下,在450—750℃温度范围内氧化50—1000小时时,这两层经历着不同的相变规律。外层是:FeAl(→Fe_3Al)→α-Fe→α-Fe+γ→γ。内层是:FeAl+β-Mn(→Fe_3Al+β-Mn)→α-Fe+β-Mn→α-Fe+β-Mn+γ→α-Fe+γ→γ。涂层的相变和涂层的退化紧密相连。贫Al的FeAl相的形成,意味着退化开始。γ的出现,称之促使退化加剧。涂层完全转变成γ,退化即告终。
Abstract:The microstructure and compositions of, and phase transformations in aluminide coating on a new Austenitic Fe-Mn-Al heat-resisting steel have been investigated in detail. Two zones were found in the coating. The outer zone is an ordered FeA1 solid solution, while the inner zone consists of FeAI, β-Mn, and V_4C_3. When this coating is oxidized in static air at 450—750℃ for 50—1000hrs, the processes of phase transformations are different in these zones. The sequence of the phase transformation in the outer zone is as follows. FeAl(→Fe_3Al)→α-Fe.→α-Fe+γ→γ, and that of the inner zone is: FeAl+β-Mn(→Fe_3Al+β-Mn)→α-Fe+β-Mn→α-Fe+β-Mn+γ→α-Fe+γ→γ. The phase transformation of the coating is closely related to the degradation of the coating. Formation of the aluminum deficient FeAl phase indicates the initiation of the coating degradation; the emergence of the γ phase means the stage of drastic degradation while the complete conversiott of the coating into γ marks the end of degradation.
收稿日期: 1982-02-25     

引用本文:

管恒荣;黄有山;楼翰一;白林祥. 一种新型奥氏体Fe-Mn-Al耐热钢铝化物涂层相变的研究[J]. 中国腐蚀与防护学报, 1982, 2(1): 11-17.
. AN INVESTIGATION OF PHASE TRANSFORMATION IN ALUMINIDE COATING OF A NEW AUSTENITIC Fe—Mn—Al HEAT—RESISTING STEEL. J Chin Soc Corr Pro, 1982, 2(1): 11-17.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y1982/V2/I1/11

[1] 一种新奥氏体热强钢-Fe-Mn-Al(918,918A)的研究,中国科学院金属研究所、抚顺钢厂、泸东造船厂。(未发表)
[2] J. H. Nickells, Metallurgia, 75, 448 (1967)
[3] D. R. Gobe, Principles of Metal surface Treatment and production, pargamon press, (1972)
[4] C. Cykes, and J. W. Bampfylde, The J. of the Iron and steel Institute, vol CⅩⅩⅩ, No. Ⅱ 389 (1934)
[5] Pavel Grobner, Hutnicke listy, 10, (1955)
[6] L. N. larikov, V. M. Falchenko, Protective Coatings on metals, 3, 66(1971)
[7] 管恒荣、黄有山、楼翰一、白林祥,Fe-Mn-Al耐热钢的氧化与防护(未发表)
[8] A. Taylor and R. M. Jones, Phys. Chem. Solids, 6, 16-37(1958)
[9] -253℃低温用钢15锰26铝4钢资料汇编,冶金工业部金属研究所,26(1974)
[10] D. J. Schmatz, Trans. AIME. 215, 112(1959)
[11] H. J. Mcqueen, G. C. Kuczynski, Trans. AIME. 215, 619(1959)
No related articles found!