化学镀Ni-B合金镀层性能

中国腐蚀与防护学报

2011, Vol. 31

Issue (4): 315-318

研究报告

本期目录 | 过刊浏览

化学镀Ni-B合金镀层性能

邝刘伟¹,范希梅¹,郝军²,张会广¹

1. 西南交通大学材料学院材料先进技术教育部重点实验室成都 610031
2. 吉林石油集团有限责任公司基建处松原 138000

STUDY ON THE PROPERTIES OF ELECTROLESS Ni-B

KUANG Liuwei¹, FAN Ximei¹, HAO Jun², ZHANG Huiguang¹

1. Key Laboratory of Advanced Technologies of Materials of Ministry of Education, Southwest Jiaotong University, Chengdu 610031
2. Construction Department, Petro-China Jilin Oilfield Company, Songyuan 138000

全文: PDF(1656 KB)

摘要: 通过改变镀液还原剂的含量和加入定量的乙酸钠，研究对化学镀镍硼合金形貌和性能的变化。从晶体结构、镀层形貌、硬度和耐磨曲线等几方面来分析加入乙酸钠12 g/L时，化学镀 Ni-B合金镀层形貌和性能改善的原因。乙酸钠起到缓冲剂的作用，降低了化学镀Ni-B的镀速，提高了化学镀Ni-B的致密度，改善了镀层的质量从而提高镀层的各种性能。

关键词 ：化学镀Ni-B, 晶体结构, 表面形貌, 磨损

Abstract：In order to enhance the properties of electroless Ni-B, the changes in morphology and performance of electroless Ni-B alloy was studied by changing the contents of reducing agent and adding quantitative sodium acetate. The reasons of the morphology and performance of the electroless Ni-B were improved while adding sodium acetate 12 g/L are analyzed based on crystal structure, coating morphology, hardness, wear curves. It was found that sodium acetate as a buffer can reduce the deposition rate of the chemical plating Ni-B, increase the density of the chemical plating Ni-B, and improve the quality of coating in the process

Key words： electroless Ni-B crystal structure coating morphology wear

收稿日期: 2010-06-22

ZTFLH:

TG 153.1

基金资助:

西南交通大学科技发展基金项目（2007B08）和吉林油田公司科技项目资助

通讯作者: 范希梅 E-mail: xmfan@swjtu.edu.cn

Corresponding author: FAN Ximei E-mail: xmfan@swjtu.edu.cn

作者简介: 邝刘伟，男，1983年生，硕士生，研究方向为材料表面技术

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	邝刘伟
44.8K

引用本文:

邝刘伟,范希梅,郝军,张会广. 化学镀Ni-B合金镀层性能[J]. 中国腐蚀与防护学报, 2011, 31(4): 315-318.
KUO Liu-Wei. STUDY ON THE PROPERTIES OF ELECTROLESS Ni-B. J Chin Soc Corr Pro, 2011, 31(4): 315-318.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I4/315

[1] Gawrilov G G. Chemical (Electroless) Nickel-Plating [M]. Redhill:Portcullis Press Limited, 1979, 529-539

[2] Mallory G O, Hajdu J B. Electroless Plating Fundamentals and Applications [M]. Florida: AESF. 1990, 252-256

[3] Riedel W. Electroless Nickel Plating, Metals Park [M]. Ohio: ASM International, 1991, 48-181

[4] Krishnavenia K, Sankara N T S N, Seshadri S K. Electroless Ni-B coatings: preparation and evaluation of hardness and wear resistance [J].Surf. Coat. Technol., 2005, 190(1): 115-121

[5] Lo Y L, Hwang B J. Kinetics of ethanol oxidation on electroless Ni-Pt/SnO₂Ti electrodes in KOH solutions [J]. Electrochem. Soc.,1995, 142(2): 445-450

[6] Gorbunova K M, Ivanov M V, Moiseev V P. Electroless deposition of nickel-boron alloys: mechanism of process, structure, and some properties of deposit [J]. J. Electrochem. Soc., 1973, 120(5): 613-618

[7] Baurand D W. ASM Handbook (Surface Engineering 5- Electroless Plating) [M]. ASM, 1994: 290

[8] Delaunois F, Lienard P. Heat treatments for electroless nickel-boron plating on aluminium alloys [J]. Surf. Coat. Technol., 2002, 160(2): 239-248

[9] Wang D Q, Shi Z Y, Zou L J. A liquid aluminum corrosion resistance surface on steel substrate [J]. Appl. Surf. Sci., 2003, 214(1): 304-311

[10] Krishnaveni K, Sankara N T S N. Electroless Ni--P/Ni-B duplex coatings: preparation and evaluation of microhardness, wear and corrosion resistance [J]. Surf. Coat. Technol., 2003, 82(3): 771-779

[11] Suo Y Z. Composite Deposits and Technical Deposits [M]. Beijing:Chemical Industry Press, 2008: 26

(索玉柱. 复合镀镍和特种镀镍 [M]. 北京：化学工业出版社，2008: 26)

[1]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[2]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[3]	陈嘉晨,王忠维,乔利杰,岩雨. 机械摩擦磨损与电化学腐蚀在特殊环境中的作用机制[J]. 中国腐蚀与防护学报, 2019, 39(5): 404-410.
[4]	余仁强,何建军,李微,任延杰,杨旺. 火电厂循环泵叶轮材料Cr30A在脱硫浆液腐蚀环境中的交互损伤失效行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 353-358.
[5]	陈磊,裴志亮,肖金泉,宫骏,孙超. 磁过滤电弧离子镀制备TiAlN涂层的结构与性能表征[J]. 中国腐蚀与防护学报, 2017, 37(3): 241-246.
[6]	陶永奇,刘刚,黎业生,曾志翔. 海水环境下2024铝合金腐蚀磨损性能研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 587-594.
[7]	刘胤, 刘时美, 于鲁萍, 刘军, 姜伟. 镁合金的腐蚀与微弧氧化膜层研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 99-105.
[8]	陈君, 李全安, 张清, 王建章, 阎逢元. AISI 316不锈钢腐蚀磨损交互作用的研究[J]. 中国腐蚀与防护学报, 2014, 34(5): 433-438.
[9]	裴和中,尹作升,张国亮,刘远勇. 2024与2124铝合金电偶腐蚀行为的对比研究[J]. 中国腐蚀与防护学报, 2012, 32(2): 133-136.
[10]	汪广进,潘牧. IrO₂复合涂层电极的研究进展[J]. 中国腐蚀与防护学报, 2012, 32(2): 85-89.
[11]	吴俊升;李晓刚;公铭扬;张志华;郭金涛. 几种催化裂化催化剂的磨损机制与动力学[J]. 中国腐蚀与防护学报, 2010, 30(2): 135-140.
[12]	王蕾胡道春. C/C复合材料抗电弧侵蚀性能研究[J]. 中国腐蚀与防护学报, 2009, 29(3): 235-240.
[13]	胡道春孙乐民上官宝. 动载荷条件下紫铜/铬青铜受流摩擦磨损性能[J]. 中国腐蚀与防护学报, 2009, 29(1): 35-39.
[14]	李红梅; 刘杏; 蔡珣; 杨武 . 304奥氏体不锈钢离子辐照后再活化性能测试和表面形貌观察[J]. 中国腐蚀与防护学报, 2006, 26(1): 37-42 .
[15]	斯松华 . 激光功率对WCp / Ni基金属陶瓷涂层的组织与磨损性能的影响[J]. 中国腐蚀与防护学报, 2004, 24(3): 183-187 .

Viewed

Full text

Abstract

Cited

Shared

Discussed