基于纳米催化剂耗氧机制的主动防腐环氧涂层构筑及性能研究
|
|
程孟, 李晓伟, 胡松青
|
Preparation and Performance of Active Anti-corrosion Epoxy Coatings Based on Oxygen Consumption Mechanism of Nano Catalysts
|
|
CHENG Meng, LI Xiaowei, HU Songqing
|
|
表1 本研究与已发表工作的对比
|
Table 1 Comparison between our work and previously published papers
|
|
| Coating | Implementation manner | Protection period /d | Ref. |
|---|
| M-ZIF-8/GO/EP | Stimuli-responsive nanocontainer | 60 | [20] | | EP/CaFe-TTA LDH@gC3N4 | Ion exchange nanocontainer | 60 | [28] | | SH/NH2-ZIF-7@AMT/PVB | Stimuli-responsive nanocontainer | 60 | [29] | | GASM | Stimuli-responsive nanocontainer | 40 | [30] | | BTA@ZIF-8@tannic acid/EP | Stimuli-responsive nanocontainer | 20 | [31] | | EP-n (Fe-N-C) | Nanocatalytic anticorrosion | 30 | [32] | | EP-n | Nanocatalytic anticorrosion | 60 | Our work |
|
|
|