含砂3.5%NaCl溶液中90°弯管冲刷腐蚀损伤机制研究
胡宗武1(
), 刘建国2, 王钰3, 李楷1
), 刘建国2, 王钰3, 李楷1
Erosion-corrosion Failure Mechanism of 90° Elbow in 3.5%NaCl Solution Containing Sand
HU Zongwu1(), LIU Jianguo2, WANG Yu3, LI Kai1
), LIU Jianguo2, WANG Yu3, LI Kai1
图9. 弯管上典型位置试样清除腐蚀产物后的冲刷腐蚀宏观形貌
Fig.9. Macroscopic erosion-corrosion morphologies of specimens at 90° (a1-g1) and 270° (a2-g2) circumferential angle of the location on the elbow after corrosion product removal