热镀锌层合金相的耐蚀性差异研究
韩宇1, 徐松1, 华思然1, 赵鹏2, 王晓杰3, 夏晓健3, 张俊喜1(
)
)
Corrosion Behavior in 3.5%NaCl Solution of Constituent Phases of Hot-dip Galvanized Coating
HAN Yu1, XU Song1, HUA Siran1, ZHAO Peng2, WANG Xiaojie3, XIA Xiaojian3, ZHANG Junxi1()
)
图2. 3种相试样在3.5%NaCl溶液中浸渍14 d的EIS图
Fig.2. EIS plots of three phases impregnated in 3.5%NaCl solution for 14 d: (a-c) δ phase, (d-f) ζ phase, (g-i) η phase