FeCrAl表面氧化对氘渗透性能影响研究
高士鑫1,2, 尹春雨1,2, 巫英伟1(
), 黄洪涛3, 张坤2, 何梁2, 叶天舟2, 陈平2
), 黄洪涛3, 张坤2, 何梁2, 叶天舟2, 陈平2
Effect of Surface Oxidation on Deuterium Permeation Performance of a Ferritic FeCrAl Alloy at 300-550 ℃
GAO Shixin1,2, YIN Chunyu1,2, WU Yingwei1(), HUANG Hongtao3, ZHANG Kun2, HE Liang2, YE Tianzhou2, CHEN Ping2
), HUANG Hongtao3, ZHANG Kun2, HE Liang2, YE Tianzhou2, CHEN Ping2
图9. 360 ℃测试后样品表面元素的XPS价态分析
Fig.9. XPS valence state analysis of sample surface elements after testing at 360 ℃: (a) valence state analysis of Cr, (b) valence state analysis of Fe, (c) valence state analysis of O