高强度低合金厚钢板在模拟海洋大气环境中的腐蚀行为
胡聪怀1, 周雯1(
), 徐正兴1, 张弦1, 张莉芹1, 张开广2, 许可3, 吴开明1
), 徐正兴1, 张弦1, 张莉芹1, 张开广2, 许可3, 吴开明1
Corrosion Behavior of High Strength Low Alloy Thick Steel Plates in Simulated Marine Atmospheric Environment
HU Conghuai1, ZHOU Wen1(), XU Zhengxing1, ZHANG Xian1, ZHANG Liqin1, ZHANG Kaiguang2, XU Ke3, WU Kaiming1
), XU Zhengxing1, ZHANG Xian1, ZHANG Liqin1, ZHANG Kaiguang2, XU Ke3, WU Kaiming1
图6. 高强度低合金厚钢板不同部位中性盐雾腐蚀实验后锈层截面形貌
Fig.6. Cross-sectional morphologies of rust layer on surface (a-c) and center (d-f) of high strength low alloy thick steel plates after different durations of neutral salt spray test: (a, d) 24 h, (b, e) 72 h, (c, f) 168 h