C/SiC复合材料的高温自对偶摩擦磨损行为及机制
王姗姗1,2, 庞生洋2, 梁斌2, 高禩洋2, 张伟3, 樊俊铃3, 张帆1, 胡成龙2, 汤素芳2(
)
)
High-temperature Friction- and Wear-behavior for Friction-pairs of Identical C/SiC Composite
WANG Shanshan1,2, PANG Shengyang2, LIANG Bin2, GAO Siyang2, ZHANG Wei3, FAN Junling3, ZHANG Fan1, HU Chenglong2, TANG Sufang2()
)
图5. 网胎针刺C/SiC复合材料在不同实验环境温度下的磨损表面形貌和EDS分析
Fig.5. Surface morphologies of needle-punched nonwoven C/SiC composites before (a) and after friction and wear tests at 25 ℃ (b), 200 ℃ (c, d), 400 ℃ (e-f), 500 ℃ (g, h), and EDS result for the area marked by the solid line box in Fig.5h (i)