增材制造与铸造钛铝合金的微观组织及高温氧化行为对比研究 |
|||||||||
| 祝丁丁, 赵希雅, 张晓美, 梅子期, 逯文君, 王帅 | |||||||||
|
Comparative Characterization of Microstructure and High-temperature Oxidation Behavior of Additive Manufacturing and Casting TiAl Alloy |
|||||||||
| ZHU Dingding, ZHAO Xiya, ZHANG Xiaomei, MEI Ziqi, LU Wenjun, WANG Shuai | |||||||||
| 表2 图7中铸造与增材制造TNM合金在900 ℃氧化24 h后局部区域(红点处)的化学成分 (atomic fraction / %) |
|||||||||
| Table 2 Chemical compositions of the local areas shown in Fig.7 (red dot regions) for the cast and AM TNM alloys after oxidation at 900 oC for 24 h |
|||||||||
|
|||||||||