ZnAlCe-NO2 水滑石@硅烷涂层的氯离子捕获和响应缓蚀行为
Chloride Ion Capture and Responsive Corrosion Inhibition Behavior of ZnAlCe-NO2 Hydrotalcite @ Silane Coating
ZnAlCe-NO2 水滑石@硅烷涂层的氯离子捕获和响应缓蚀行为 |
| 谭敬莎, 郭艺超, 陈俊霖, 盖文峰, 孟国哲 |
|
Chloride Ion Capture and Responsive Corrosion Inhibition Behavior of ZnAlCe-NO2 Hydrotalcite @ Silane Coating |
| TAN Jingsha, GUO Yichao, CHEN Junlin, GAI Wenfeng, MENG Guozhe |
| 图3 碳钢在添加ZnAlCe-NO2 LDH溶液中的Bode和Nyquist图。碳钢在NaCl (0.05 mol/L)溶液与添加ZnAlCe-NO2 LDH的NaCl (0.05 mol/L)混合溶液中浸泡不同时间后的极化曲线图及EIS拟合的等效电路模型 |
| Fig.3 Bode plots (a, b) and Nyquist plots (c) of carbon steel in ZnAlCe-NO2 LDH-containing solution. Polarization curves of carbon steel after immersion in 0.05 mol/L NaCl blank solution and 0.05 mol/L NaCl solution containing ZnAlCe-NO2 LDH for different durations: 24 h (d) and 48 h (e). Equivalent circuit models (a, b) for EIS fitting (f) |
|
|