选区激光熔化奥氏体不锈钢高温高压水中应力腐蚀开裂行为研究进展
Research Progress of Stress Corrosion Crack Behavior of Selected Laser Melted Austenitic Stainless Steel in High Temperature Pressurized Water
选区激光熔化奥氏体不锈钢高温高压水中应力腐蚀开裂行为研究进展 |
| 兰博韬, 吴斌, 明洪亮, 王俭秋, 韩恩厚 |
|
Research Progress of Stress Corrosion Crack Behavior of Selected Laser Melted Austenitic Stainless Steel in High Temperature Pressurized Water |
| LAN Botao, WU Bin, MING Hongliang, WANG Jianqiu, HAN En-Hou |
| 图5 SLM材料制备过程中产生的气孔和层状空隙[ |
| Fig.5 Pores (a) and layered voids (b) generated during SLM material preparation process[ |
|
|