低温扩散预处理对含B超级奥氏体不锈钢S31254析出相及耐蚀性的影响
Effect of Low Temperature Diffusion Pretreatment on Precipitation of Phases During Post-aging Treatment for B-containing S31254 Super Austenitic Stainless Steel and its Corrosion Resistance
低温扩散预处理对含B超级奥氏体不锈钢S31254析出相及耐蚀性的影响 |
| 何燕, 刘燕, 田华, 陈晔 |
|
Effect of Low Temperature Diffusion Pretreatment on Precipitation of Phases During Post-aging Treatment for B-containing S31254 Super Austenitic Stainless Steel and its Corrosion Resistance |
| HE Yan, LIU Yan, TIAN Hua, CHEN Ye |
| 图6 经300 ℃保温处理不同时间、再经900 ℃时效处理2 h后S31254钢的动电位再活化曲线 |
| Fig.6 Potentiodynamic reactivation curves of S31254 steel with isothermal treatment at 300 oC for different time and then aging at 900 oC for 2 h in 10%NaCl solution |
|
|