热处理对激光选区熔化GH4099镍基高温合金900 ℃下(75%Na2SO4 + 25%NaCl)热腐蚀行为的影响
Effect of Heat Treatment on Hot Corrosion Behavior of Selective Laser Melted GH4099 Nickel-based Superalloy Beneath (75%Na2SO4 + 25%NaCl) Deposits in Air at 900 oC
热处理对激光选区熔化GH4099镍基高温合金900 ℃下(75%Na2SO4 + 25%NaCl)热腐蚀行为的影响 |
| 白英雄, 王艳丽, 李相伟, 吴泽峰, 张书彦 |
|
Effect of Heat Treatment on Hot Corrosion Behavior of Selective Laser Melted GH4099 Nickel-based Superalloy Beneath (75%Na2SO4 + 25%NaCl) Deposits in Air at 900 oC |
| BAI Yingxiong, WANG Yanli, LI Xiangwei, WU Zefeng, ZHANG Shuyan |
| 图3 SLM GH4099和HT GH4099在900 ℃下75% Na2SO4 + 25%NaCl混合盐膜中热腐蚀120 h的质量变化曲线 |
| Fig.3 Mass change curves of SLM GH4099 and HT GH4099 during hot corrosion in 75%Na2SO4 + 25%NaCl mixed salt deposit at 900 oC for 120 h |
|
|