B30铜镍合金原始膜对其腐蚀的影响

王立芳, 商孟超, 高希钰, 刘贵昌, 孙文

Effect of Inherent Films Resulted from Manufacturing Process on Corrosion of B30 Cu-Ni Alloy

WANG Lifang, SHANG Mengchao, GAO Xiyu, LIU Guichang, SUN Wen

表7 图12中Mott-Schottky曲线拟合结果

Table 7 Fitting results of Mott-Schottky curves in Fig.12

Samples Slope p Slope n NA / cm-3 ND / cm-3 A sample -8.42 × 1011 5.18 × 1011 2.36 × 1019 1.92 × 1019 B sample -9.47 × 109 8.07 × 109 2.10 × 1021 1.23 × 1021 C sample -6.43 × 1013 - 4.83 × 1017 -