模拟液滴电导率变化对碳钢大气腐蚀的影响机制研究

李兆南, 侯禹岑, 莒鹏, 庄铁钢, 陈景杰, 王明昱, 徐云泽

Influence of Simulated Electrolyte Droplets with Varied Conductivity on Atmospheric Corrosion of Carbon Steel

LI Zhaonan, HOU Yucen, JU Peng, ZHUANG Tiegang, CHEN Jingjie, WANG Mingyu, XU Yunze

图5 不同浓度液滴下腐蚀不同时期的丝束表面形貌图和末期电流分布图

Fig.5 Surface morphologies of the wire beam at the initial (a1-d1), final (a2-d2) and after rust removal (a3-d3) corrosion stages under droplets with 0.001 mol/L (a), 0.003 mol/L (b), 0.2 mol/L (c) and 0.5 mol/L (d) concentration and current distribution maps at the end corrosion stage (a4-d4)