CO2-CO气氛下3.5%硅钢固态脱碳氧化层演变规律

CO₂-CO气氛下3.5%硅钢固态脱碳氧化层演变规律

孙伶艳, 洪陆阔, 孙彩娇, 艾立群, 周美洁, 闻莉

Evolution of Oxide Scale of 3.5% Silicon Steel in Solid State Decarburization in CO₂-CO Atmospheres

SUN Lingyan, HONG Lukuo, SUN Caijiao, AI Liqun, ZHOU Meijie, WEN Li

图14 P $_{C O_{2}}$ /P_CO = 0.10条件下脱碳时硅钢试样表面氧化层形貌演变

Fig.14 Cross-sectional morphologies of oxide scale formed on 3.5% silicon steel after decarburization at P $_{C O_{2}}$ /P_CO = 0.10 for different time: (a) 10 min, (b) 20 min, (c) 30 min, (d) 40 min, (e) 50 min, (f) 60 min