CO2 压力对含杂质超临界CO2 输送管线X65钢应力腐蚀开裂敏感性的影响
Effect of CO2 Pressure on Stress Corrosion Cracking Susceptibility of X65 Pipeline Steel Used for Transporting Impure Supercritical CO2
CO2 压力对含杂质超临界CO2 输送管线X65钢应力腐蚀开裂敏感性的影响 |
| 程璐瑶, 徐彦磊, 李家玮, 孙冲, 林学强, 孙建波 |
|
Effect of CO2 Pressure on Stress Corrosion Cracking Susceptibility of X65 Pipeline Steel Used for Transporting Impure Supercritical CO2 |
| CHENG Luyao, XU Yanlei, LI Jiawei, SUN Chong, LIN Xueqiang, SUN Jianbo |
| 图7 在不同压力的含杂质超临界CO2环境中施加520 MPa应力并暴露240 h后X65管线钢的应力腐蚀速率 |
| Fig.7 Corrosion rate of X65 pipeline steel with the stress of 520 MPa exposed to supercritical CO2 environment containing impurities at different CO2 pressures for 240 h |
|
|