CO2 压力对含杂质超临界CO2 输送管线X65钢应力腐蚀开裂敏感性的影响
Effect of CO2 Pressure on Stress Corrosion Cracking Susceptibility of X65 Pipeline Steel Used for Transporting Impure Supercritical CO2
CO2 压力对含杂质超临界CO2 输送管线X65钢应力腐蚀开裂敏感性的影响 |
| 程璐瑶, 徐彦磊, 李家玮, 孙冲, 林学强, 孙建波 |
|
Effect of CO2 Pressure on Stress Corrosion Cracking Susceptibility of X65 Pipeline Steel Used for Transporting Impure Supercritical CO2 |
| CHENG Luyao, XU Yanlei, LI Jiawei, SUN Chong, LIN Xueqiang, SUN Jianbo |
| 图5 在含杂质超临界CO2环境中不同CO2压力下X65管线钢的断面收缩率(Ψ)和SCC敏感性因子(IΨ-SCC) |
| Fig.5 Reduction-in-area (Ψ) (a) and SCC susceptibility index (IΨ-SCC) (b) of X65 pipeline steel after SSRT test in impurity-containing supercritical CO2 environment at different CO2 pressures |
|
|