钛基体阴极充氢处理对RuO2-IrO2-TiO2 阳极微观结构和性能的影响

刘鹏鹤, 薛丽莉, 许立坤, 辛永磊, 郭明帅, 周帅, 段体岗

Effect of Hydrogen Pre-charging for Ti-substrate on Microstructure and Electrochemical Properties of Ti/RuO2-IrO2-TiO2 Anode

LIU Penghe, XUE Lili, XU Likun, XIN Yonglei, GUO Mingshuai, ZHOU Shuai, DUAN Tigang

图10 钛基体未充氢和经不同电流密度充氢后制备的氧化物阳极在1 mol/L硫酸溶液中强化电解加速寿命测试(电流密度为1 A/cm2)时的槽压随时间的变化

Fig.10 Cell voltage vs. time curves recorded during accelerated life tests in 1 mol/L sulfuric acid solution at 1 A/cm2 for the oxide anodes prepared on titanium substrates uncharged and charged with hydrogen at different current densities