海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment
海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究 |
| 张国庆, 余直霞, 王岳松, 王智, 金正宇, 刘宏伟 |
|
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment |
| ZHANG Guoqing, YU Zhixia, WANG Yuesong, WANG Zhi, JIN Zhengyu, LIU Hongwei |
| 图9 A106钢在不同温度下超临界CO2环境中暴露5 d后并去除腐蚀产后的二维和三维表面形貌图以及对应的腐蚀坑深度变化曲线图 |
| Fig.9 Two-dimension (a, d, g) and three-dimension (b, e, h) surface morphologies of the specimens and the corresponding curves of corrosion pits (c, f, i) after removing the corrosion products formed during exposure for 5 d in sc-CO2 environment containing 2000 μL/L H2O at 25 ℃ (a-c), 60 ℃ (d-f) and 100 ℃ (g-i) |
|
|