海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment
海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究 |
| 张国庆, 余直霞, 王岳松, 王智, 金正宇, 刘宏伟 |
|
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment |
| ZHANG Guoqing, YU Zhixia, WANG Yuesong, WANG Zhi, JIN Zhengyu, LIU Hongwei |
| 图5 A106钢在35 ℃不同含水量的超临界CO2环境中暴露5 d且去除表面腐蚀产物后的局部形貌图 |
| Fig.5 Surface morphologies of A106 steel after removing the corrosion products formed during exposure at 35 ℃ for 5 d in sc-CO2 environments containing 200 μL/L (a-c), 1000 μL/L (d-f), 1500 μL/L (g-i), 2000 μL/L (j-l), 2500 μL/L (m-o) and 3000 μL/L (p-r) H2O |
|
|