海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment
海上超临界二氧化碳环境中含水率和温度对A106钢腐蚀行为影响研究 |
| 张国庆, 余直霞, 王岳松, 王智, 金正宇, 刘宏伟 |
|
Corrosion Behavior of Steel Materials in Marine Supercritical Carbon Dioxide Environment |
| ZHANG Guoqing, YU Zhixia, WANG Yuesong, WANG Zhi, JIN Zhengyu, LIU Hongwei |
| 图3 A106钢在35 ℃不同含水量的超临界CO2环境中暴露5 d后的SEM表面腐蚀产物形貌和EDS分析 |
| Fig.3 SEM images (a1-f1) and corresponding EDS analysis results (a2-f2) of the corrosion products formed on A106 steel after exposure at 35 ℃ in sc-CO2 environments containing 200 μL/L (a1, a2), 1000 μL/L (b1, b2), 1500 μL/L (c1, c2), 2000 μL/L (d1, d2), 2500 μL/L (e1, e2) and 3000 μL/L (f1, f2) H2O |
|
|