水化学对690镍基合金高温高压水腐蚀行为的影响
Effect of Water Chemistry on Corrosion Behavior of Nickel-based Alloy 690 in High Temperature High Pressure Water
水化学对690镍基合金高温高压水腐蚀行为的影响 |
| 李顺平, 党莹, 洪晓峰, 宁方强 |
|
Effect of Water Chemistry on Corrosion Behavior of Nickel-based Alloy 690 in High Temperature High Pressure Water |
| LI Shunping, DANG Ying, HONG Xiaofeng, NING Fangqiang |
| 图2 690合金在290 ℃不同水化学参数的高温水中浸泡500 h后氧化膜的SEM形貌 |
| Fig.2 SEM morphologies of oxide scales formed on alloy 690 after 500 h exposure at 290 ℃ in water with different water chemistries: (a1, a2) 3 mg/L DO, (b1, b2) 1 μg/L DO, (c1, c2) 3 mg/L DH |
|
|