退火工艺对304奥氏体不锈钢的组织演变及氢脆行为的影响

张慧云, 郑留伟, 梁伟

Effect of Annealing Process on Microstructure Evolution and Hydrogen Embrittlement Behavior of 304 Austenitic Stainless Steel

ZHANG Huiyun, ZHENG Liuwei, LIANG Wei

图2 冷轧态以及700 ℃下1 min和3 min退火态样品的IPF图和相分布图

Fig.2 IPF maps (a, c, e) and phase distribution maps (b, d, f) of CR-20% (a, b), 700 oC-1 min (c, d) and 700 oC-3 min (e, f) samples