氢对2205双相不锈钢在3.5%NaCl溶液中缝隙腐蚀行为影响
Effect of Hydrogen on Crevice Corrosion Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution
氢对2205双相不锈钢在3.5%NaCl溶液中缝隙腐蚀行为影响 |
| 汤熠鑫, 张飞, 崔中雨, 崔洪芝, 李燚周 |
|
Effect of Hydrogen on Crevice Corrosion Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution |
| TANG Yixin, ZHANG Fei, CUI Zhongyu, CUI Hongzhi, LI Yizhou |
| 图3 3.5%NaCl溶液中2205双相不锈钢在不同充氢时间下的动电位极化曲线及其相应的点蚀击穿电位和钝化电流密度 |
| Fig.3 Potentiodynamic polarization curves of 2205 duplex stainless steel in 3.5%NaCl solution after hydrogen charging for different time (a), and their corresponding pitting breakdown potentials (Ebp) and passivation current densities (Ip) (b) |
|
|