H2 中O2 和CO掺杂对X52管线钢氢脆敏感性影响研究
Effect of Small Amount of O2 and CO on Hydrogen Embrittlement Susceptibility of X52 Pipeline Steel
H2 中O2 和CO掺杂对X52管线钢氢脆敏感性影响研究 |
| 万红江, 明洪亮, 王俭秋, 韩恩厚 |
|
Effect of Small Amount of O2 and CO on Hydrogen Embrittlement Susceptibility of X52 Pipeline Steel |
| WAN Hongjiang, MING Hongliang, WANG Jianqiu, HAN En-Hou |
| 图14 在掺入0.02%CO的H2气氛中试样断口形貌 |
| Fig.14 Fracture morphologies of X52 pipeline steel in H2 atmosphere containing 0.02%CO: (a) general view, (b-d) magnified images of the regions A, B, and C marked in Fig.14a, respectively |
|
|