H2 中O2 和CO掺杂对X52管线钢氢脆敏感性影响研究
Effect of Small Amount of O2 and CO on Hydrogen Embrittlement Susceptibility of X52 Pipeline Steel
H2 中O2 和CO掺杂对X52管线钢氢脆敏感性影响研究 |
| 万红江, 明洪亮, 王俭秋, 韩恩厚 |
|
Effect of Small Amount of O2 and CO on Hydrogen Embrittlement Susceptibility of X52 Pipeline Steel |
| WAN Hongjiang, MING Hongliang, WANG Jianqiu, HAN En-Hou |
| 图5 在掺入不同含量O2的H2气氛中试样的拉伸断口整体形貌 |
| Fig.5 Overall fracture morphologies of X52 pipeline steel in H2 atmospheres containing 0% (a), 0.001% (b), 0.005% (c), and 0.01% (d) O2 |
|
|