激光增材制造AlCoCrFeNiSi高熵合金的氧化行为 |
郭静波, 杨守华, 周子翼, 牟仁德, 谢云, 舒小勇, 戴建伟, 彭晓 |
High-temperature Oxidation Behavior of Laser Additively Manufactured AlCoCrFeNiSi High Entropy Alloy |
GUO Jingbo, YANG Shouhua, ZHOU Ziyi, MU Rende, XIE Yun, SHU Xiaoyong, DAI Jianwei, PENG Xiao |
图2 700 W与900 W激光功率下沉积的Al0.21Co0.17Cr0.13Fe0.11Ni0.18Si0.20腐刻后微观形貌与晶粒大小分布图,(a)中插图为放大图像 |
Fig.2 Morphologies (a, b) and grain size distributions (c, d) of Al0.21Co0.17Cr0.13Fe0.11Ni0.18Si0.20 manufactured by LMD at 700 W (a, c) and 900 W (b, d). The inset in Fig.2a is a magnified image |
![]() |