搪瓷涂层在600 ℃熔融MgCl2-NaCl-KCl中热腐蚀行为研究

杨啸东, 李雪, 喻政, 杨莎莎, 陈明辉, 王福会

Corrosion Behavior of Enamel Coatings in Molten Salts MgCl2-KCl-NaCl at 600 oC

YANG Xiaodong, LI Xue, YU Zheng, YANG Shasha, CHEN Minghui, WANG Fuhui

表2 图6中各区域的元素成分分析 (atomic fraction / %)

Table 2 EDS analyses of the regions marked with 1-5 in Fig.6

Position O Si Mg Al Ca Sr Co Na K Cl 1 65.95 8.85 20.46 1.18 0.43 0.93 0 0.51 0.87 0.83 2 45.67 30.71 9.41 2.26 2.58 3.01 0.35 2.62 2.25 1.15 3 57.23 23.77 10.74 2.67 1.06 2.14 0.21 0.65 1.14 0.39 4 63.40 11.26 22.28 0.86 0.25 0.77 0.01 0.35 0.30 0.50 5 53.74 26.77 9.37 3.14 1.80 3.18 0.20 0.84 0.74 0.24