搪瓷涂层在600 ℃熔融MgCl2-NaCl-KCl中热腐蚀行为研究
Corrosion Behavior of Enamel Coatings in Molten Salts MgCl2-KCl-NaCl at 600 oC
搪瓷涂层在600 ℃熔融MgCl2-NaCl-KCl中热腐蚀行为研究 |
| 杨啸东, 李雪, 喻政, 杨莎莎, 陈明辉, 王福会 |
|
Corrosion Behavior of Enamel Coatings in Molten Salts MgCl2-KCl-NaCl at 600 oC |
| YANG Xiaodong, LI Xue, YU Zheng, YANG Shasha, CHEN Minghui, WANG Fuhui |
| 图3 搪瓷涂层在600 ℃下MgCl2-KCl-NaCl熔盐中热腐蚀500 h前后的宏观形貌 |
| Fig.3 Macro images of B12 (a, d), B15 (b, e) and B18 (c, f) enamel coatings before (a-c) and after (d-f) hot corrosion in MgCl2-KCl-NaCl molten salt at 600 oC for 500 h |
|
|