典型氟橡胶密封材料热空气老化试验研究 |
刘明, 张连栋, 孙志华, 高蒙, 闫巍, 赵明亮 |
Assessment on Performance Decay Induced by Hot Air Aging for Typical Fluoroelastomer Sealing Materials |
LIU Ming, ZHANG Liandong, SUN Zhihua, GAO Meng, YAN Wei, ZHAO Mingliang |
图13 热空气老化试验后典型氟橡胶FX-17的拉伸断口表面的元素含量 |
Fig.13 Mass fraction of various elements on the tensile fracture surface of typical fluoroelastomer FX-17 after hot air aging tests |
![]() |