K444合金表面CVD渗铝涂层耐高温95%Na2SO4 + 5%NaCl腐蚀行为研究
Corrosion Resistance of CVD Aluminized Coating on K444 Alloy Beneath a Thin Deposits of 95%Na2SO4 + 5%NaCl at High Temperature
K444合金表面CVD渗铝涂层耐高温95%Na2SO4 + 5%NaCl腐蚀行为研究 |
| 王粤, 耿树江, 王金龙, 王福会, 孙清云, 吴勇, 夏思瑶 |
|
Corrosion Resistance of CVD Aluminized Coating on K444 Alloy Beneath a Thin Deposits of 95%Na2SO4 + 5%NaCl at High Temperature |
| WANG Yue, GENG Shujiang, WANG Jinlong, WANG Fuhui, SUN Qingyun, WU Yong, XIA Siyao |
| 图9 K444合金在950 ℃、Na2SO4 + NaCl条件下腐蚀10 h的SEM截面形貌及EDS点分析 |
| Fig.9 SEM cross-sectional morphology with EDS point analysis of K444 alloy with deposit of Na2SO4 + NaCl at 950 oC after 10 h corrosion |
|
|