静水压力对Cr/GLC叠层涂层腐蚀行为的影响
马宏宇, 刘叡, 崔宇, 柯培玲, 刘莉, 王福会

Effect of Hydrostatic Pressure on Corrosion Behavior of Cr/GLC Laminated Coating
MA Hongyu, LIU Rui, CUI Yu, KE Peiling, LIU Li, WANG Fuhui
图3 0.1 MPa和 15 MPa压力下服役不同时间后Cr/GLC叠层涂层表面腐蚀形貌
Fig.3 Surface morphologies of multilayer Cr/GLC laminated coating after immersion for 48 h (a, b) and 168 h (c, d) at 0.1 MPa (a, c) and 15 MPa (b, d)